- Hexcel® HexPly® F522 Epoxy Resin, F3C584 Carbon Fabric
Hexcel® HexPly® F522 Epoxy Resin, F3C584 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F522 Epoxy Resin, F3C584 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: F3C584-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 820 MPa @Temperature 24.0 °C |
119000 psi @Temperature 75.2 °F |
Dry |
| Tensile Modulus | 72.4 GPa @Temperature 24.0 °C |
10500 ksi @Temperature 75.2 °F |
Dry |
| Compressive Yield Strength | 655 MPa @Temperature 24.0 °C |
95000 psi @Temperature 75.2 °F |
Dry |
| Compressive Modulus | 66.9 GPa @Temperature 24.0 °C |
9700 ksi @Temperature 75.2 °F |
Dry |
| Shear Strength | 63.4 MPa @Temperature 24.0 °C |
9200 psi @Temperature 75.2 °F |
Short Beam, Dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Dry Resin Content (%) | 37-41 | Prepreg |
| Fiber Volume (%) | 0.038 | Laminate |
| Flow (%) | 11-23 | |
| Wet Resin Content (%) | 52 | Laminate |
Users viewing this material also viewed the following:
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Paraplex G25
- M. Holland Company CP420 Polypropylene Impact Copolymer
- Tra-Con Tra-Bond FDA2YL02 Food and Drug Application Epoxy Adhesive
- A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene
- Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Conditioned, 23% Glass Filled
- 3M Scotch® 2622 Repulpable Box Sealing Tape
- HP Alloys Alloy X, 15% Cold Worked
- EG65D-B20 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved