- RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Body side moldingsGrillesElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 28 % | 28 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 23.0 °C |
3.00 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 13.6 J | 10.0 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Polymer Resources PPX/NY G20 Modified PPO, 20% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l
- Magyar Aluminum ALO-DF223 Alumina
- Teknor Apex Tekbond® TB 1158C Thermoplastic Elastomer
- Zircar Refractory Composites Alumina Coat
- EMS-Grivory Grivory® TSK-30/4 PA666-GB30
- DSM Akulon® K224-G3 (Cond.) 15% Glass Reinforced Nylon 6 (North America)
- Atom Adhesives AA-GREASE 04 Epoxy Adhesive
- Axiall 15640 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved