- Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK) (Unverified Data**)
Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire AV-722 CF30 is a 30% carbon fiber reinforced version of AvaSpire AV-722. This formulation offers improved part economics relative to 30% carbon fiber reinforced PEEK while retaining most of the desirable high performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-722 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, oil and gas and chemical processing. The melt processing behavior of AV-722 CF30 is overall very similar to that of 30% CF reinforced PEEK.Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber Reinforcement |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Viscosity | 470000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
470000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm @Thickness 3.18 mm |
0.00 - 0.0020 in/in @Thickness 0.125 in |
5" x 0.5" x 0.125" bars; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Thickness 3.18 mm |
0.014 - 0.016 in/in @Thickness 0.125 in |
5" x 0.5" x 0.125" bars; ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 400 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 107 | 107 | M-Scale; ASTM D785 |
| Tensile Strength | 200 MPa | 29000 psi | 5.0 mm/min; ASTM D638 |
| Tensile Strength, Yield | 224 MPa | 32500 psi | ISO 527-2/1A/5 |
| Elongation at Break | 1.5 % | 1.5 % | 5.0 mm/min; ASTM D638 |
| 1.5 % | 1.5 % | ISO 527-2/1A/5 | |
| Tensile Modulus | 22.0 GPa | 3190 ksi | 5.0 mm/min; ASTM D638 |
| 26.6 GPa | 3860 ksi | ISO 527-2/1A/1 | |
| Flexural Strength | 304 MPa | 44100 psi | ASTM D790 |
| 334 MPa | 48400 psi | ISO 178 | |
| Flexural Modulus | 19.3 GPa | 2800 ksi | ASTM D790 |
| 25.0 GPa | 3630 ksi | ISO 178 | |
| Compressive Strength | 170 MPa | 24700 psi | ASTM D695 |
| Poissons Ratio | 0.44 | 0.44 | ASTM E132 |
| Shear Modulus | 7.64 - 9.24 GPa | 1110 - 1340 ksi | Calculated |
| Shear Strength | 98.0 MPa | 14200 psi | ASTM D732 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 5.30 J/cm | 9.93 ft-lb/in | ASTM D4812 | |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature -50.0 - 50.0 °C |
3.33 µin/in-°F @Temperature -58.0 - 122 °F |
TMA; ASTM E831 |
| Specific Heat Capacity | 1.28 J/g-°C @Temperature 50.0 °C |
0.306 BTU/lb-°F @Temperature 122 °F |
DSC |
| 1.74 J/g-°C @Temperature 200 °C |
0.416 BTU/lb-°F @Temperature 392 °F |
DSC | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | Peak (major component); ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Mold Temperature | 177 - 204 °C | 351 - 399 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Flame Retardant | |
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| High Heat Resistance | ||
| High Stiffness | ||
| High Strength | ||
| Forms | Pellets | |
| Generic | PAEK | |
| Injection Rate | Fast | |
| Processing Method | Injection Molding | |
| Machining | ||
| Profile Extrusion | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | |
| Uses | Automotive Applications | |
| Gears | ||
| Industrial Applications |
Users viewing this material also viewed the following:
- MV Labs NI650 {Ni(NH3)6}I2 Hexaminenickel(II) iodide
- Kraton® D1116 E (SBS) Radial Triblock Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF0335 PC (Europe-Africa-Middle East)
- ChevronTexaco Drive Train Fluid HD, SAE 30
- Fainplast Compounds KL 90/2 Flexible PVC, Insulation for High Temperatures Lead Free
- Cheng Yu Plastic FR200GV10 Flame Retardant Nylon 66, 10% Glass Fiber
- Westlake Hifor Xtreme SC74860-F Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved