- SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High productivityGood optical propertiesContains 1600 ppm slip agent and 1900 ppm antiblocking agentRecommended Applications:Film for heavy duty bag, industrial bag, rice bag, sugar bag, frozen bagAgricultural filmConstruction filmInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.919 g/cc | 0.919 g/cc | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour @Temperature 50.0 °C |
>= 1000 hour @Temperature 122 °F |
F50, 25% Igepal; ASTM D1639 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 1050 % | 1050 % | ASTM D882 |
| Film Elongation at Break, TD | 810 % | 810 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 5.71 g/micron | 145 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 370 g/mil | ASTM D1922 |
| Dart Drop | 3.40 g/micron | 86.4 g/mil | ASTM D1709 |
| Dart Drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 °C | 252 °F | ASTM D2117 |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 18 % | 18 % | ASTM D1003 |
| Gloss | 51 % | 51 % | ASTM D2457 |
Users viewing this material also viewed the following:
- MV Labs TM800 Tm2O3 Thulium oxide
- PolyOne Edgetek® SY-15GB/000 Polystyrene (PS), Glass Bead Filled (discontinued **)
- Solvay Specialty Polymers Polymist® F-5A EX PTFE Powder Lubricant (Unverified Data**)
- Overview of materials for Polytetrafluoroethylene (PTFE), Mica Filled
- Lord Adhesives Metech 3540 Platinum Silver Conductor Composition
- Techmer ES HiFill® PA6 GF/B20 A2 20% Glass Fiber/Glass Bead Filled
- SABIC Innovative Plastics LNP Thermocomp PH0600B PA 6
- Zylog Neoplast® 187 FT EB Thermoplastic Vulcanizate
- Cotronics Resbond™ 906 High Temperature Ceramic Adhesive, High Expansion
- ExxonMobil LDPE LD 200.48 Low Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved