PTS Tristar® PC-10FRN 15 MFI Flame Retardant Polycarbonate With Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Tristar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Tristar® PC-10FRN 15 MFI Flame Retardant Polycarbonate With Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ASTM D792
Water Absorption 0.18 %
0.18 %
24 hours at 73°F; ASTM D570
Melt Flow 15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 62.1 MPa

@Thickness 3.17 mm
 9000 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 75 %

@Thickness 3.17 mm
 75 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 89.6 MPa

@Thickness 3.17 mm
 13000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.21 GPa

@Thickness 3.17 mm
 320 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 5.87 J/cm

@Thickness 3.17 mm
 11.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Tensile Impact Strength 443 kJ/m²

@Thickness 3.17 mm
 211 ft-lb/in²

@Thickness 0.125 in
 ASTM D1822
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.2 µm/m-°C

@Temperature -40.0 - 95.0 °C
 39.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
CTE, linear, Transverse to Flow 68.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 38.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 134 °C
273 °F
ISO 75
UL RTI, Electrical 125 °C
257 °F
UL RTI, Mechanical with Impact 115 °C
239 °F
UL RTI, Mechanical without Impact 125 °C
257 °F
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 2.50 mm
 5VA

@Thickness 0.0984 in
 Black, Gray, Beige
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
Oxygen Index 37.6 %
37.6 %
ASTM D2863
Glow Wire Test 775 °C
1430 °F
GWIT
960 °C
1760 °F
GWFI
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
PLC 6
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC 2
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 1.50 mm
 15 - 30 sec

@Thickness 0.0591 in
 PLC 3
15 - 30 sec

@Thickness 2.50 mm
 15 - 30 sec

@Thickness 0.0984 in
 PLC 3
30 - 60 sec

@Thickness 3.00 mm
 30 - 60 sec

@Thickness 0.118 in
 PLC 2
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 2.50 mm
 60 - 120 arcs

@Thickness 0.0984 in
 PLC 1
60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 PLC 1
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC 3
Processing Properties Metric English Comments
Rear Barrel Temperature 254 - 274 °C
490 - 525 °F
Middle Barrel Temperature 266 - 277 °C
510 - 530 °F
Front Barrel Temperature 277 - 293 °C
530 - 560 °F
Nozzle Temperature 271 - 293 °C
520 - 560 °F
Melt Temperature 282 - 304 °C
540 - 580 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Injection Pressure 75.8 - 124 MPa
11000 - 18000 psi
Back Pressure 0.345 - 1.38 MPa
50.0 - 200 psi
Descriptive Properties Value Comments
Edge Gate Slow to Medium
Tab Gate Medium to Fast
Tunnel Gate Fast