- Polymer Property : Melt Flow = 15 g/10 min
Polymer Property : Melt Flow = 15 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ASTM D1238 |
|
RheTech Products RCC233-01 33% Calcium Carbonate Reinforced Polypropylene Copolymer, Black, Recycled Content
Applications: Fender linersSplash shieldsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ASTM D1238 |
|
RheTech Products T40P100-00A 40% Talc Reinforced Polypropylene, Natural
Applications: Durable goodsHVAC componentsFunctional supportsElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Melt Flow |
15
-
30
g/10 min <br>@Load 2.16 kg,<br> Temperature 210 °C
|
15
-
30
g/10 min <br>@Load 4.76 lb,<br> Temperature 410 °F
|
ASTM D1238 |
|
NatureWorks® Ingeo™ 6201D Fiber Grade PLA
NatureWorks® PLA polymer 6201D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6201D is designed for extrusion into mechanically ..
|
|||
| Melt Flow |
15
-
20
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
-
20
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ASTM D1238/L |
|
NIZHNEKAMSKNEFTEKHIM PP 1500P (V30G) Propylene Homopolymer
Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P..
|
|||
| Melt Flow |
15
-
25
g/10 min <br>@Load 11.6 kg,<br> Temperature 250 °C
|
15
-
25
g/10 min <br>@Load 25.6 lb,<br> Temperature 482 °F
|
ASTM D1238 |
|
Polymer Resources PPX-FR5 Modified-PPO, V-0 Flame Retardant
Modified-Polyphenylene Oxide, V-0 Flame Retardant, 225F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-..
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ISO 1133 |
|
Solvay Engineered Polymers DEXFLEX® 990 TPO
(discontinued **)
Description: DEXFLEX® 990 is a thermoplastic olefinic elastomer (TPO) designed for automotive exterior applications that require a combination of stiffness, low-temperature impact, and excellent pr..
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | melt index; ASTM D1238 |
|
Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads
(discontinued **)
25% glass beads-filled grade with superior isotropic dimensional stability.Applications: Speedometer frames.This product is not a part of the standard product line dated 2003.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 10.0 kg,<br> Temperature 380 °C
|
15
g/10 min <br>@Load 22.0 lb,<br> Temperature 716 °F
|
|
|
Lehmann & Voss LUVOCOM® 1105-7741 PEEK, with mineral filler, lubricant modified
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
|
Global PC-1415-R General Purpose Polycarbonate
Information provided by Global Polymers Corporation.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
|
Kotec Carbotex KFR-30 Polycarbonate, Flame Retardant
Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Multibase Multibatch® MP 53663 Sheet Extrusion
CPP. 70% CaCO3 Filled.Impact Resistant.Information provided by Multibase
|
|||
| Melt Flow |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
|
SABIC Innovative Plastics PC1500 PC (Europe-Africa-Middle East)
PC1500 resin is a medium-high flow (MFR = 15 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rel..
|
|||
| Melt Flow | 15 - 25 g/10 min | 15 - 25 g/10 min | ASTM D1238 |
|
Shuman 930-05V0 White Polycarbonate Glass Filled
Easy processability, heat resistance, weatherability, color stability, self extinguishing5% glass fiber for foam moldingInformation provided by Shuman Plastics, Inc.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238; ISO 1133 |
|
Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin
Overview: CALIBREâ„¢ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding ..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 280 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 536 °F
|
ASTM D1238 |
|
SABIC Innovative Plastics NORYL N1150 PPE+PS (Asia Pacific)
Noryl* N1150 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow, this resin also uses non-chlorinated, non-brominated FR add..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F
|
ASTM D1238 |
|
A. Schulman POLYBATCH™ Beige 1266E Concentrate Based In Polyethylene
DescriptionPOLYBATCH® 1266E is a beige color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH®..
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ISO 1133 |
|
Tisan TISOPLEN® 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Polypropylene
TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
|
A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene
DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 275 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 527 °F
|
ISO 1133 |
|
Polyram RamLloy PFS302G14 ASA/PBT Alloy, 14% Glass Fiber
14% Glass fiber reinforced ASA/PBT alloy for injection molding applications.Information provided by Polyram.
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
|
A. Schulman POLYFORT™ FPP 1239H Glass Filled Chemically Coupled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1239H is a 30% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 330 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 626 °F
|
|
|
Covestro Apec® HT KU 1-9340/5 High-Heat Polycarbonate
Transparent and opaque shades possible, easy-to-demold.Applications: Medical sector: superheated steam sterilization.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was s..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
ExxonMobil Exxtral™ LNU 012 Performance Polyolefin
Product Description: A specialty thermoplastic polyolefin resin with good heat resistance and good surface finish designed for fast injection molding of large electrical appliance parts.Availability..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C
|
15
g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F
|
ASTM D1238 |
|
Diamond Polymers PC 2109T Natural, UV Stabilized, Flame Retardant Polycarbonate
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F
|
ASTM D1238 |
|
E-Polymers Tekaloy® G70F2 G70NH, Non-Halogen Flame Retardant, Un-Reinforced PC/ABS Alloy
V-2, High FlowInformation provided by E-Polymers Co. Ltd.
|
|||
| Melt Flow |
15
-
25
g/10 min <br>@Load 5.00 kg,<br> Temperature 230 °C
|
15
-
25
g/10 min <br>@Load 11.0 lb,<br> Temperature 446 °F
|
ASTM D1238 |
|
E-Polymers EFLEX® M500 SEBS
M-series: E-FLEX M series resins are a maleic anhydride grafted (MAH) polymer concentrate designed as synthetic rubber and polyolefin manufactured by E-Polymers. It offers excellent adhesion to nyl..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 235 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 455 °F
|
after drying; ISO 1133 |
|
Arkema Group Orgalloy® RS 6600 Polyamide 6.6 Alloy
Polyamide Alloy, Rigid grade, Nylon 6.6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
|
|||
| Melt Flow |
15
g/10 min <br>@Load 5.00 kg,<br> Temperature 372 °C
|
15
g/10 min <br>@Load 11.0 lb,<br> Temperature 702 °F
|
ASTM D1238 |
|
3M Dyneon™ PFA 6910GZ Fluoroplastic Dispersion
3M™ Dyneon™ PFA 6910GZ is a 50% solids fluorothermoplastic aqueous dispersion. It is a copolymer of tetrafluoroethylene and perfluorinated comonomers, with a melt viscosity several orders of magni..
|
|||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
|
Washington Penn Polypropylene Copolymer 20% Glass Reinforced, 15 MFI
Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. ..
|
|||
| Melt Flow |
15
g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C
|
15
g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F
|
ISO 1133 |
|
Polyram RamOfin PPC359T4 Polypropylene, 20% Mineral Filled
20% mineral filled, heat stabilized and impact modified for polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Melt Flow | 15 - 19 g/10 min | 15 - 19 g/10 min | ASTM D1238 |
|
Buckeye Polymers BP FLEX D5518 R 848 Thermoplastic Polyolefin
Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist..
|
|||