- Multibase Multi-Pro® 1004 R Polypropylene
Multibase Multi-Pro® 1004 R Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 1004 R Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Scratch Resistance, GoodHeat Resistance, HighStiffness, GoodForms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.3 MPa | 5700 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 260 °C | 390 - 500 °F | |
| Middle Barrel Temperature | 204 - 260 °C | 400 - 500 °F | |
| Front Barrel Temperature | 216 - 260 °C | 420 - 500 °F | |
| Nozzle Temperature | 216 - 249 °C | 420 - 480 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® AS-30CF/000 UV Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (discontinued
- Fine Organics FINALUX G 411 Lubricant Additive
- Garlock 9780 Fluoroelastomer Sheet Rubber Gasketing
- Teknor Apex Chemlon® 100 Nylon 66, Unreinforced
- Samsung Cheil Industries Infino® HX-4300G PPA, Glass Filled
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Dow SE SLR-4400 Solution polymerized Styrene Butadiene Rubber (S-SBR)
- Colorite Polymers 8512 Clear Injection Molding Vinyl Compound
- Industeel UREA 25.22.2 Plants
Copyright © lookpolymers.com All Rights Reserved