Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Multibase
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Multibase

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70	70	molded- without post cure; ASTM D2240
	72	72	post cured- 4 hours at 177Â°C; ASTM D2240
	73	73	post cured- 2 hours at 177Â°C; ASTM D2240
	75	75	post cured- 8 hours at 177Â°C; ASTM D2240
Tensile Strength, Ultimate	7.58 MPa	1100 psi	molded-without post cure; ASTM D412
	7.58 MPa	1100 psi	post cured- 2 hours at 177Â°C; ASTM D412
	7.58 MPa	1100 psi	post cured- 4 hours at 177Â°C; ASTM D412
	7.58 MPa	1100 psi	post cured- 8 hours at 177Â°C; ASTM D412
Tensile Strength, Yield	3.86 MPa	560 psi	at 200%, molded-without post cure; ASTM D412
	4.14 MPa	600 psi	200%, post cured- 4 hours at 177Â°C; ASTM D412
	4.14 MPa	600 psi	at 200%, post cured- 2 hours at 177Â°C; ASTM D412
	4.55 MPa	660 psi	200%, post cured- 8 hours at 177Â°C; ASTM D412
Elongation at Break	460 %	460 %	post cured- 8 hours at 177Â°C; ASTM D412
	500 %	500 %	post cured- 2 hours at 177Â°C; ASTM D412
	500 %	500 %	post cured- 4 hours at 177Â°C; ASTM D412
	560 %	560 %	molded-without post cure; ASTM D412
Tear Strength	36.8 kN/m	210 pli	Die B, post cured- 8 hours at 177Â°C; ASTM D624
	40.3 kN/m	230 pli	Die B,molded-without post cure; ASTM D624
	40.3 kN/m	230 pli	Die B,post cured- 2 hours at 177Â°C; ASTM D624
	42.1 kN/m	240 pli	Die B, post cured- 4 hours at 177Â°C; ASTM D624
Compression Set	61 %	61 %	22 hours at 177Â°C, post cured- 4 hours at 177Â°C; ASTM D395
	74 %	74 %	22 hours at 177Â°C, molded-without post cure; ASTM D395
	75 %	75 %	22 hours at 177Â°C, post cured- 8 hours at 177Â°C; ASTM D395
	80 %	80 %	22 hours at 177Â°C, post cured- 2 hours at 177Â°C; ASTM D395

Thermal Properties	Metric	English	Comments
Shrinkage	2.90 % @Temperature 177 Â°C, Time 14400 sec	2.90 % @Temperature 351 Â°F, Time 4.00 hour	post cured
	3.00 % @Temperature 177 Â°C, Time 7200 sec	3.00 % @Temperature 351 Â°F, Time 2.00 hour	post cured
	3.50 % @Temperature 177 Â°C, Time 28800 sec	3.50 % @Temperature 351 Â°F, Time 8.00 hour	post cured