- MRC Polymers SATRANâ„¢ 800R ABS Terpolymer, Reprocessed
MRC Polymers SATRANâ„¢ 800R ABS Terpolymer, Reprocessed
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | MRC Polymers |
| Trade Name | SATRAN™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MRC Polymers SATRANâ„¢ 800R ABS Terpolymer, Reprocessed.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
black onlyInformation provided by MRC Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.0 - 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 - 4.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
nominal; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 - 216 °C | 380 - 420 °F | |
| Middle Barrel Temperature | 199 - 221 °C | 390 - 430 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 204 - 227 °C | 400 - 440 °F | |
| Melt Temperature | 204 - 227 °C | 400 - 440 °F | |
| Mold Temperature | 26.7 - 60.0 °C | 80.0 - 140 °F | function of wall thickness |
| Drying Temperature | 76.7 - 87.8 °C | 170 - 190 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour | |
| Moisture Content | <= 0.040 % | <= 0.040 % | |
| Dew Point | -28.9 °C | -20.0 °F | |
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 40 - 75 % | 40 - 75 % | |
| Cushion | 0.330 - 0.813 cm | 0.130 - 0.320 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fill Rate | Moderate | |
| Hold Pressure | 40-60% of injection pressure | |
| Packing Pressure | 50-75% of injection pressure | |
| Screw Speed | Slow |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID: 50-80/5-15 nm Aligned Multi-Walled Carbon Nanotubes
- Fibre Glast Duratec 1040 Clear Hi-Gloss Gel Coat Additive
- Loxim 841 02T HB Polypropylene Compound, 40% Talc Filled, Flame Retardant
- Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, As Conditioned
- Styron EMERGEâ„¢ 4330-15 Polycarbonate
- SABIC Innovative Plastics LNP STAT-LOY WF306C PBT
- Westlake Tymax™ GT4157 Anhydride Modified Linear Low Density Polyethylene
- Formosa Plastics Formolene® HP6000 Pipe HDPE
- 3M 7122 Performance Paper Label Material
- Aremco Corr-Paint™ CP4040-S1 High Temperature Protective Coating, Silicone
Copyright © lookpolymers.com All Rights Reserved