Addiplast Addinyl A2 V40 Nylon 66, 40% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl A2 V40 Nylon 66, 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, high strengthInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | Conditioned; ISO 868 |
| 86 | 86 | ISO 868 | |
| Tensile Strength at Break | 160 MPa | 23200 psi | Conditioned; ISO R 527 |
| 210 MPa | 30500 psi | ISO R 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO R 527 |
| 4.0 % | 4.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 7.70 GPa | 1120 ksi | Conditioned; ISO 178 |
| 10.5 GPa | 1520 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180/1A |
| 17.0 kJ/m² | 8.09 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/IeU |
| 7.50 J/cm² | 35.7 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/IeA |
| 1.60 J/cm² | 7.61 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM E831 |
| Melting Point | 260 °C | 500 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2/AF |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; CEI 60243-1 |
| 35.0 kV/mm | 889 kV/in | CEI 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced
- LG Chemical HIPS MI730 PS, Impact Modified
- ITW Plexus Plexusâ„¢ MA330 Methacrylate Adhesive
- Schott DURAN® Borosilicate Glass
- Taiwan PU Corporation TPUI-E98 General Grade, Injection Molding Polyester Base TPU
- Skamol Group SKAMOCAST 112-80 Insulating Castable
- Arlon 0.015" (0.381 mm) Flexible Heater Silicone with Fiberglass Substrate (51941C015)
- Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced
- Bulk Molding Compounds BMC 845 30% Glass Filled Vinyl Ester
- Momentive Performance Materials HV 3/606 Heat Cured Rubber - High Temperature
Copyright © lookpolymers.com All Rights Reserved