- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 85.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 85.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-1 |
| Mytex Polymers AS33L-16 Polypropylene, Rubber modified, Talc filled, Compounded Description: AS33L-16 is a compounded, talc, rubber modified polypropylene for exterior automotive applications. Material has outstanding moldability and excellent balance of high stiffness and goo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| RheTech Products RCC233-01 33% Calcium Carbonate Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: Fender linersSplash shieldsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS (Europe-Africa-Middle East) Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties for a wide variety of applications including business equipment, TVs, monitors, enclosures, among others.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa LONOY 1600 PC/PBT Alloy Features:Excellent balance propertiesGood weather resistanceGood size stabilitySmooth surfaceUniform colorApplications:Injection moldingAutomobile bumperAutomobile interior/exterior trim partsBusine.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-3302 TO BU Elastomer Modified, UV-Stabilized Polypropylene Block-Copolymer INNOPOL® CS 2-3302 TO BU is an elastomer modified, UV-stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3302 TO BU is developed for producing injection molded automotive.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Ineos N20N-00 Polypropylene Impact Copolymer This is a high melt flow rate, nucleated polypropylene impact copolymer formulated for improved flowability. It has an optimum balance of stiffness and impact resistance for injection molded applic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer (Asia Pacific) LUBRICOMP* YL-4030 CCS is a PTFE Lubricated Compound based on Polyester Elastomer resin which has low ionic and low outgassing performance for the Semicon and Internal Hard Disk Drive applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
ASTM D648 |
| A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Borealis BE170MO Polypropylene Copolymer BE170MO is a heterophasic copolymer. This grade is characterized by high impact strength, high stiffness and good flow properties. This grade contains additives providing low taste and odor as well.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene DescriptionPolypropylene PP 1500X-01 is a specially formulated high impact copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Borealis Daplen™ EF005AE Polypropylene TPO Compound Daplen™ EF005AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, give.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman PP 1116-01 Polypropylene Molding Grade Copolymer Polypropylene DescriptionPolypropylene PP 1116-01 is a molding grade copolymer polypropylene with improved low temperature toughness and good room temperature toughness. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene DescriptionPolyflam® RPP 1021 is a general purpose copolymer polypropylene flame retardant material with a UL V-2 flammability rating and 105°C temperature index at 0.030 in.Information provided b.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Formosa Plastics Formolene® 2510A Injection Applications Polypropylene Impact Copolymer with Nucleating, Antistat AdditivesApplications: Closures, housewares, small appliances, battery cases and lids.Formolene 2510A is a medium impact copolymer of polypropylene charact.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman PP 1579 Polypropylene Impact Grade Polypropylene DescriptionPolypropylene PP 1579 is an impact grade of polypropylene for use in parts which require good impact and good appearance in light weight injection molded parts. Information provided by A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Eastman Tenite 383A4000011 Cellulose Acetate Propionate, Clear, Trsp Applications:AppliancesFloor carePersonal care and cosmeticsProfilesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, stren.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Eastman Tenite 550E3V45510 Cellulose Acetate Butyrate, Water Clear, Trsp Applications:AppliancesConsumer-Personal careProfilesProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gl.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Eastman Tenite Butyrate 285A3720010 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Hytrel® HTR8241 TPC-ET
(Unverified Data**) Hytrel® HTR8241 is a 65 nom.Shore D, non discoloring stabilizer, plasticiser free high performance resin for extrusion; high viscosity; outstanding mechanical properties up to 120°C and excellent .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| BASF Novolen® 1100 RC Polypropylene, Injection Molding Grade Injection molded partsData was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| BASF Novolen® 1101 M Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Tipco Tipcolene® MD-TPE MD TPE - Impact Modified Polypropylene Copolymer Compound for Automobile Bumpers High Impact PP CopolymerApplications: Automotive BumpersProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| BASF Novolen® 1101 N Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| BASF Novolen® 1102 J Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | Unannealed; ISO 75B-1, -2 |
| LyondellBasell Hifax™ HSBMCB1158LS Thermoplastic Polyolefin Elastomer Description: Hifax™ HSBMCB1158LS high melt flow, 1,200 MPa flexural modulus, mineral filled thermoplastic elastomeric olefin (TEO) resin has a unique balance of flow, rigidity, low temperature impa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1021 General Purpose Copolymer Polypropylene DescriptionPolyflam® RPP 1021 is a general purpose copolymer polypropylene flame retardant material with a UL V-2 flammability rating and 105°C temperature index at 0.030 in.Information provided b.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene DescriptionPolyflam® RPP 1360 is a UL 94 V0 rated, non-halogenated homopolymer polypropylene flame retardant compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Formosa Plastics Formolene® 2620A Impact Copolymer Polypropylene Impact Copolymer for Compounding and Injection Molded Applications Formolene® 2620A is a high impact copolymer of polypropylene designed for applications such as automotive compounds and lawn & gar.. |
|||