Lanxess Durethan® AKV 40 H3.0 000000 Nylon 66, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 40 H3.0 000000 Nylon 66, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
PA 66, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ISO 1183
Moisture Absorption at Equilibrium 1.7 %
1.7 %
50% RH; ISO 62
Water Absorption at Saturation 4.5 %
4.5 %
ISO 62
Linear Mold Shrinkage, Flow 0.00030 cm/cm
0.00030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0036 cm/cm
0.0036 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.00090 cm/cm
0.00090 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0092 cm/cm
0.0092 in/in
60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
cond.; ISO 527-1, -2; 5 mm/min
220 MPa
31900 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
5.0 %
5.0 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 1.30 GPa
189 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
8.80 GPa
1280 ksi
cond.; ISO 527-1, -2; 1 mm/min
Flexural Strength 240 MPa

@Strain 5.00 %
 34800 psi

@Strain 5.00 %
 cond., 2 mm/min; ISO 178-A
330 MPa

@Strain 4.00 %
 47900 psi

@Strain 4.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 210 MPa

@Strain 3.50 %
 30500 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 8.00 GPa
1160 ksi
cond., 2 mm/min; ISO 178-A
11.7 GPa
1700 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
14.0 kJ/m²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
9.50 J/cm²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
1.20 J/cm²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Tensile Creep Modulus, 1 hour 7700 MPa
1.12e+6 psi
cond.; ISO 899-1
Tensile Creep Modulus, 1000 hours 6800 MPa
986000 psi
cond.; ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 262 °C
504 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1, -2
Vicat Softening Point >= 230 °C

@Load 5.10 kg
 >= 446 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Glow Wire Test 600 °C

@Diameter 2.00 mm
 1110 °F

@Diameter 0.0787 in
 GWIT; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
d.a.m.; IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
4.9

@Frequency 100 Hz
 4.9

@Frequency 100 Hz
 d.a.m.; IEC 60250
Dielectric Strength 40.0 kV/mm

@Thickness 1.00 mm
 1020 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Dissipation Factor 0.026

@Frequency 1.00e+6 Hz
 0.026

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
0.027

@Frequency 100 Hz
 0.027

@Frequency 100 Hz
 d.a.m.; IEC 60250
Comparative Tracking Index 575 V
575 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
290 °C
554 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 66, MHR, 14-120, GF40