Industrial Laminates/Norplex NP130 Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP130 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Woven glass fabric combined with a halogenated epoxy resin system. Produced to printed circuit board quality standards. Flame retardant, meets UL-94 flammability classification V-0.Thickness Tested: 0.0620", 0.125" & 0.500".
Physical Properties Metric English Comments
Specific Gravity 1.75 - 1.85 g/cc

@Thickness 1.57 mm
 1.75 - 1.85 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.15 %

@Thickness 1.57 mm
 0.15 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 262 MPa

@Thickness 1.57 mm
 38000 psi

@Thickness 0.0620 in
 CW; ASTM D638
310 MPa

@Thickness 1.57 mm
 45000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 16.5 GPa

@Thickness 1.57 mm
 2400 ksi

@Thickness 0.0620 in
 CW; ASTM D229
18.6 GPa

@Thickness 1.57 mm
 2700 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 414 MPa

@Thickness 1.57 mm
 60000 psi

@Thickness 0.0620 in
 CW; ASTM D790
483 MPa

@Thickness 1.57 mm
 70000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 379 MPa

@Thickness 12.7 mm
 55000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 152 MPa

@Thickness 15.7 mm
 22000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 6.41 J/cm

@Thickness 12.7 mm
 12.0 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
7.47 J/cm

@Thickness 12.7 mm
 14.0 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 5.56 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 12.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 6.67 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 140 °C
284 °F
Glass Transition Temp, Tg 127 °C
261 °F
Tg
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 4.8

@Thickness 1.57 mm
 4.8

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 29.5 kV/mm

@Thickness 1.57 mm
 750 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
31.5 kV/mm

@Thickness 1.57 mm
 800 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 54000 V

@Thickness 1.57 mm
 54000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
65000 V

@Thickness 1.57 mm
 65000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.025

@Thickness 1.57 mm
 0.025

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 100 sec

@Thickness 3.17 mm
 100 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 150 V

@Thickness 3.17 mm
 150 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 2200 lb
0.5", ASTM D229
Color Natural, Black