Polymer Property : Flexural Modulus = 8.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	8.00 - 12.0 GPa	1160 - 1740 ksi	Compression; ISO 178
Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically..
Flexural Modulus	8.00 - 10.0 GPa	1160 - 1450 ksi	Injection; ISO 178
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets..
Flexural Modulus	8.00 - 12.0 GPa	1160 - 1740 ksi	Injection and Compression; ISO 178
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Flexural Modulus	8.00 - 18.0 GPa	1160 - 2610 ksi	Average value: 13.1 GPa Grade Count:26
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled". Each property range of values repor..
Flexural Modulus	8.00 - 12.0 GPa	1160 - 1740 ksi	Injection and Compression; ISO 178
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m..
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Hexion Bakelite™ PF 12404 Phenolic Formaldehyde Resin, High Surface Quality, Low Shrinkage (discontinued **)& Phenolic molding compound, inorganically/organically filled, good dimensional stability, low shrinkage.Application areas: Housing parts for gas meter.Information provided by Bak AGBak AG became a pa..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8053/EM/BL PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 21-7976 Polyamide 6/6T, with glass fiber and PTFE, 8-mm-granulate Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 2205-7054 Blend based on polyaryl ether ketone, with glass fiber Applications: High dimensionally stable precision parts, high continuous use temperature.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceChemical and hydr..
Flexural Modulus	8.00 GPa @Temperature 22.0 Â°C	1160 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 1650 Unsaturated Polyester UP SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in ..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Loxim 230 01HB Polybutylene Terephthalate Information provided by Loxim Industries
Flexural Modulus	8.00 GPa	1160 ksi
Lehmann & Voss LUVOCOMÂ® 80-8072 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Modulus	8.00 GPa @Temperature 22.0 Â°C	1160 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® SMC 0420 Unsaturated Polyester UP SMC 0420 is a low density Premium Class-A SMC for exterior body applications on cars, LCVÂ´s and trucks. These compounds mould to light weight parts with good up to excellent surface quality for ..
Flexural Modulus	8.00 GPa	1160 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 420 PBT (Europe-Africa-Middle East) VALOX 420 is a 30% glass fiber reinforced PBT injection moulding resin with excellent mechanical and thermal properties. Applications: appliance handles, spotlights, electric motors.
Flexural Modulus	8.00 GPa	1160 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® K4560 PBT 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable.
Flexural Modulus	8.00 GPa	1160 ksi	2mm/min; ISO 178
Teijin Multilon DN-1530B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 30 % filler. Improved stiffness and high fluidity realizes a thin wall..
Flexural Modulus	8.00 GPa	1160 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN3 PPE+PS PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Sui..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek PB300G33 Nylon 6, 33% Glass Fiber 33% glass fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM-D790
Polyram PlusTek RA303G6 Nylon 6.6, 30% Glass Fiber 30% glass fiber reinforced, heat stabilized, and hydrolysis resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	8.00 GPa	1160 ksi	2 mm/min; ISO 178
Eurostar Starflam AFR450X2 PA66, 25% Glass Filled, Injection Molded AFR450X2 is a Red Phosphorous, Flame Retardant, 25% Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive su..
Flexural Modulus	8.00 GPa	1160 ksi	2 mm/min; ISO 178
Eurostar Staramide BG6 PA6, 30% Glass Filled, Injection Molded BG6 is a 30% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
A. Schulman ComAlloy E-13370B Internally Lubricated, Glass Fiber Reinforced Polyester Alloy Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
A. Schulman ComAlloy Hiloy® 613 Nylon 6, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	8.00 GPa	1160 ksi	ASTM D790
Beijing Chemical Industry KAIFA® 301-G30 PBT Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Modulus	8.00 GPa @Temperature 120 °C	1160 ksi @Temperature 248 °F	ASTM D790
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS) (Unverified Data**) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..