- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 482 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 482 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | STN EN ISO 75-2 (A) |
|
Plastcom SLOVAMID® 6 GF 30 AS PA6 reinforced with glass fiber, anti-static agent
PA 6 for injection molding, reinforced with 30% glass fiber, contains antistatic agent for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
|
Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
|
Nilit FRIANYL A63 N-SG5 Nylon 6.6 for injection molding, 5% mineral filled
Nylon 6.6 for injection molding, low viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
|
Nilit FRIANYL A63 W-GV15 Nylon 6.6 for injection molding, 15% glass fiber reinforced
Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
|
PTS Trimid® N66-G33L 33% Glass Fiber Reinforced Lubed Nylon 6/6
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Zytel® HTN 51G15HSL BK083 Polyphthalamide (PPA)
(Unverified Data**)
Zytel® HTN51G15HSL BK083 is a 15% glass reinforced, heat stabilized, lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polymers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
|
Lehmann & Voss LUVOCOM® 1301-8456 PPS, linear, with glass fiber, PTFE, lubricant modified
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
|
Lehmann & Voss LUVOCOM® 20-7687 Polyphthalamide, with aramid reinforcement and PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low influence from moisture an..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
|
Lanxess Durethan® AKV 35 H2.0 901510 Nylon 66, 35% Glass Fiber
PA 66, injection molding grade, 35% glass fibers, good heat-ageing resistanceApplication Examples: gearbox oil sumps, oil modules
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
|
LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized
Polyamide 66 (PA66) based compound. Oil stabilized. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
|
Lanxess Durethan® AKV 15 000000 Nylon 66, 15% Glass Fiber
PA 66, injection molding grade, 15% glass fibers
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
|
LATI Latilub 66-15T G/30 PA66, 30% Glass Fiber Reinforced, PTFE Filled
Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
|
Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant
Information from Shinkong Synthetic Fibers Corp.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RC004SXS PA 66 (Europe-Africa-Middle East)
LNP* Thermocomp* RC004SXS is a compound based on PA 66 resin containing Carbon Fiber. Added features include; Heat Stabilized, Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Thermocomp RF007S PA 66 (Europe-Africa-Middle East)
LNP* THERMOCOMP* RF007S is a compound based on PA 66 resin containing Glass Fiber . Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Unannealed; ASTM D648 |
|
Chase Plastics CP Pryme® NN133LUV (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, UV Stabilized
Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthGood UV resistanceForm: PelletsApplications: Automotive under the hoodOutd..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
|
Polyram PlusTek RA301G8 Nylon 6.6 for Injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized
Heat stabilized, 40% glass fiber reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
|
DSM Akulon® S223-HG6 (Dry) 30% Glass Reinforced Nylon 66 (North America)
Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 GV 25 HWCP 25% Glass Fiber Nylon 66, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 GV 40 HWCP 40% Glass Fiber Nylon 66, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® GVX-65 H nat PA*-GF65
Product description: Grivory GVX-65H natural is a 65% glass-fiber reinforced engineering thermoplastic material based on a combination of semi-crystalline polyamide with partially aromatic copolyami..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® TSG-50/4 W PA666-GF50
Product description: Grilon TSG-50/4 W is a high heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 50% glass fibers, modified for parts with high thermal demands. Grilon TSG-..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
|
Ensinger Tecamid® GF30 Extruded Nylon 6/6 30% glass-fiber-reinforced (PA66)
Tecamid® 6/6 GF30 is a 30% glass-fiber reinforced nylon 6/6 material whose important properties include high tensile and flexural strength, stiffness, excellent heat deflection temperature, and sup..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
|
A. Schulman ComAlloy Hiloy® 623 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL
Data provided by the manufacturer, ComAlloy International Company.33% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
|
BASF Ultramid® A3EG7 BK00564 35% Glass Filled PA66 (Dry)
Ultramid A3EG6 BK00564 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Unannealed; ISO 75-2/A |
|
Ascend Performance Materials Vydyne® R530H NAT Nylon 66, 30% Glass Reinforced, DAM
Vydyne® R530H NAT is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of ph..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-2/A |
|
Ascend Performance Materials Vydyne® R533 Nylon 66, 33% Glass Filled, Dry as Molded
Vydyne® R533 is general-purpose, 33% glass-reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for good machine feed, flow, and mold release. Glas..
|
|||