- Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced
Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 35% glass fibers, injection molding, heat-aging stabilized, improved surface finishInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00030 cm/cm | 0.00030 in/in | Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577 |
| 0.00070 cm/cm | 0.00070 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | |
| 0.0032 cm/cm | 0.0032 in/in | 60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4 | |
| 0.0035 cm/cm | 0.0035 in/in | 150x105x3; 300°C / MT 80°C; 400 bar; ISO 2577 | |
| Linear Mold Shrinkage, Transverse | 0.00040 cm/cm | 0.00040 in/in | Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577 |
| 0.00090 cm/cm | 0.00090 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | |
| 0.010 cm/cm | 0.010 in/in | 60x60x2; 300°C / MT 80°C; 600 bar; ISO 294-4 | |
| 0.014 cm/cm | 0.014 in/in | 150x105x3; 300°C / MT 80°C; 400 bar; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 190 MPa | 27600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 3.0 % | 3.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 5.0 % | 5.0 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 7.50 GPa | 1090 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 11.2 GPa | 1620 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 200 MPa @Strain 6.00 % |
29000 psi @Strain 6.00 % |
cond., 2 mm/min; ISO 178-A |
| 295 MPa @Strain 4.00 % |
42800 psi @Strain 4.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 170 MPa @Strain 3.50 % |
24700 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| Flexural Modulus | 6.70 GPa | 972 ksi | cond., 2 mm/min; ISO 178-A |
| 10.5 GPa | 1520 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
d.a.m.; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA | |
| Tensile Creep Modulus, 1 hour | 7000 MPa | 1.02e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 5800 MPa | 841000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Vicat Softening Point | >= 230 °C @Load 5.10 kg |
>= 446 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Oxygen Index | 23 % | 23 % | Method A; ISO 4589-2 |
| Glow Wire Test | 600 °C @Diameter 2.00 mm |
1110 °F @Diameter 0.0787 in |
GWIT; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | cond.; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | d.a.m.; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | cond.; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | d.a.m.; IEC 60093 | |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
cond.; IEC 60243-1 |
| 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
d.a.m.; IEC 60243-1 | |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 |
| 0.065 @Frequency 1.00e+6 Hz |
0.065 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 0.11 @Frequency 100 Hz |
0.11 @Frequency 100 Hz |
d.a.m.; IEC 60250 | |
| 0.21 @Frequency 100 Hz |
0.21 @Frequency 100 Hz |
cond.; IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| 290 °C | 554 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66, GHR, 14-110, GF35 |
Users viewing this material also viewed the following:
- Fiberfil® PP-15/T/10/20 Polypropylene Homopolymer, 22% Talc Filled
- SABIC Innovative Plastics ULTEM 1110 PEI
- Special Metals NIMONIC® Alloy 86
- Total PPC 4824WZ Polypropylene, Impact Copolymer
- Epoxy Technology EPO-TEK® E3001-HV Electrically Conductive, Silver Epoxy
- Braskem TI2350C High Crystallinity Copolymer Polypropylene
- Fainplast Compounds MPH 75/D Medical Flexible PVC, Extrusion
- PolyOne Elastamax HTE 2101-1000 Polyurethane Alloy (discontinued **)
- Loctite® Quick Metal® 660 Retaining Compound
Copyright © lookpolymers.com All Rights Reserved