Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
Manufacturer | LG Chemical |
Trade Name | Lupox® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | LG Chemical Lupox® GP2156FM PBT+GF15%.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm |
0.0040 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 95.1 MPa @Thickness 3.20 mm |
13800 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
Flexural Yield Strength | 149 MPa @Thickness 3.20 mm |
21600 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
Flexural Modulus | 5.69 GPa @Thickness 3.20 mm |
825 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
Izod Impact, Notched | 0.520 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.974 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
UL RTI, Electrical | 130 °C @Thickness >=0.710 mm |
266 °F @Thickness >=0.0280 in |
|
130 °C @Thickness >=1.50 mm |
266 °F @Thickness >=0.0591 in |
||
130 °C @Thickness >=3.00 mm |
266 °F @Thickness >=0.118 in |
||
UL RTI, Mechanical with Impact | 130 °C @Thickness >=0.710 mm |
266 °F @Thickness >=0.0280 in |
|
130 °C @Thickness >=1.50 mm |
266 °F @Thickness >=0.0591 in |
||
130 °C @Thickness >=3.00 mm |
266 °F @Thickness >=0.118 in |
||
UL RTI, Mechanical without Impact | 130 °C @Thickness >=0.710 mm |
266 °F @Thickness >=0.0280 in |
|
130 °C @Thickness >=1.50 mm |
266 °F @Thickness >=0.0591 in |
||
130 °C @Thickness >=3.00 mm |
266 °F @Thickness >=0.118 in |
||
Flammability, UL94 | V-0 @Thickness >=0.710 mm |
V-0 @Thickness >=0.0280 in |
|
V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
||
V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
Dielectric Strength | 26.0 kV/mm @Thickness 1.00 mm |
660 kV/in @Thickness 0.0394 in |
ASTM D149 |
Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | ASTM D495 |
Comparative Tracking Index | 175 V | 175 V | Solution A; IEC 60112 |
Hot Wire Ignition, HWI | 15 - 30 sec @Thickness >=0.710 mm |
15 - 30 sec @Thickness >=0.0280 in |
|
15 - 30 sec @Thickness >=1.50 mm |
15 - 30 sec @Thickness >=0.0591 in |
||
30 - 60 sec @Thickness >=3.30 mm |
30 - 60 sec @Thickness >=0.130 in |
||
High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.710 mm |
>= 120 arcs @Thickness 0.0280 in |
|
>= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
||
>= 120 arcs @Thickness 3.30 mm |
>= 120 arcs @Thickness 0.130 in |
||
High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
Melt Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
Drying Temperature | 120 °C | 248 °F | Injection Molding |
Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |