LG Chemical LUPOY SC3154 PC+GF15%

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY SC3154 PC+GF15%.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC+GF15%, General Purpose, Good Toughness, Dimensional Stability, Good Surface, Chemical ResistanceApplication: Mobile Phone Housing and ComponentsInformation provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0050 cm/cm
<br>@Thickness 3.20 mm
 0.0040 - 0.0050 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 11 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 11 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D785
Tensile Strength, Yield 47.1 MPa
<br>@Thickness 3.20 mm
 6830 psi
<br>@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 25 %
<br>@Thickness 3.20 mm
 25 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa
<br>@Thickness 3.20 mm
 12800 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 3.04 GPa
<br>@Thickness 3.20 mm
 441 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 2.16 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 4.04 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
<br>@Thickness 6.40 mm
 279 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C
<br>@Thickness >=1.70 mm
 176 °F
<br>@Thickness >=0.0669 in
80.0 °C
<br>@Thickness >=3.10 mm
 176 °F
<br>@Thickness >=0.122 in
UL RTI, Mechanical with Impact 80.0 °C
<br>@Thickness >=1.70 mm
 176 °F
<br>@Thickness >=0.0669 in
80.0 °C
<br>@Thickness >=3.10 mm
 176 °F
<br>@Thickness >=0.122 in
UL RTI, Mechanical without Impact 80.0 °C
<br>@Thickness >=1.70 mm
 176 °F
<br>@Thickness >=0.0669 in
80.0 °C
<br>@Thickness >=3.10 mm
 176 °F
<br>@Thickness >=0.122 in
Flammability, UL94 HB
<br>@Thickness >=1.70 mm
 HB
<br>@Thickness >=0.0669 in
HB
<br>@Thickness >=3.10 mm
 HB
<br>@Thickness >=0.122 in
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 295 °C
536 - 563 °F
Injection Molding
Middle Barrel Temperature 285 - 300 °C
545 - 572 °F
Injection Molding
Front Barrel Temperature 290 - 305 °C
554 - 581 °F
Injection Molding
Nozzle Temperature 290 - 305 °C
554 - 581 °F
Injection Molding
Melt Temperature 295 - 310 °C
563 - 590 °F
Injection Molding
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding