Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D-955
Melt Flow 14 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 14 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ASTM D-785
Tensile Strength, Yield 43.1 MPa
<br>@Thickness 3.20 mm
 6260 psi
<br>@Thickness 0.126 in
 Type 1; ASTM D-638
Flexural Yield Strength 66.2 MPa
<br>@Thickness 6.40 mm
 9600 psi
<br>@Thickness 0.252 in
 ASTM D-790
Flexural Modulus 2.21 GPa
<br>@Thickness 6.40 mm
 320 ksi
<br>@Thickness 0.252 in
 ASTM D-790
Izod Impact, Notched 2.75 J/cm
<br>@Thickness 6.40 mm
 5.14 ft-lb/in
<br>@Thickness 0.252 in
 ASTM D-256
3.3333 J/cm
<br>@Thickness 3.20 mm
 6.2446 ft-lb/in
<br>@Thickness 0.126 in
 ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 106 °C
223 °F
Method B; ASTM D-1525
Flammability, UL94 HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in
 UL-94