LG Chemical LUPOY GN5151RFA PC/ABS Mineral Filler
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GN5151RFA PC/ABS Mineral Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame RetardantApplication: IT&OA (Notebook PC housingCAS: 103598-77-2, 9003-56-9, 181028-79-5 and 14807-96-6Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.040 | 0.040 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.8 MPa @Thickness 3.20 mm |
8530 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 103 MPa @Thickness 3.20 mm |
14900 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 4.31 GPa @Thickness 3.20 mm |
626 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.00 - 1.10 mm |
140 °F @Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.00 - 1.10 mm |
140 °F @Thickness 0.0394 - 0.0433 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.00 - 1.10 mm |
140 °F @Thickness 0.0394 - 0.0433 in |
|
| Flammability, UL94 | V-0 @Thickness 1.00 - 1.10 mm |
V-0 @Thickness 0.0394 - 0.0433 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Injection Molding |
| Front Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Nozzle Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Melt Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 85.0 - 95.0 °C | 185 - 203 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 1.96 MPa | 142 - 284 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 72 T 40 PP, 40% mineral filling
- Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 581 Quartz Reinforced
- Arkema Group Rilsan® ARVO 950 TLD Nylon 12, Rotomolding Grade (Dry)
- BASF Heligoen® Green K 8730 Color Additive
- 3M FM283 Indoor UL Recognized White Polyester Label Products
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- Dow Corning XIAMETER® PMCPMEM-0062 Emulsion PS
- A. Schulman ComAlloy Hiloy® 621 Nylon 6/6, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved