Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf)

Category	Polymer , Adhesive , Film , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Hexcel
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported versions contain a woven nylon carrier for glueline thickness control and improved handleability. Redux 319 is a hot melt film which is free from solvents and consequently it has a very low volatile content.Features: Cures in 60 min at 350°F; Good performance at temperatures ranging from -67°F to 300°F; Good short-term exposure performance at 350°F; Excellent peel properties; Good drape at ambient temperatures; Less than 1% volatile content.Applications: Aluminum to aluminum bonding; Fiber-reinforced composite to composite bonding; Aluminum honeycomb sandwich bonding; Aramid honeycomb sandwich bonding.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	8.89 MPa @Temperature 22.2 °C	1290 psi @Temperature 72.0 °F	Flatwise Tensile
	8.998 MPa @Temperature 22.2 °C	1305 psi @Temperature 72.0 °F	Flatwise Tensile, Primed with Redux 119
Shear Strength	0.152 MPa @Temperature 149 °C	22.0 psi @Temperature 300 °F	Lap Shear Unprimed, 12 months at 300°F
	0.207 MPa @Temperature 22.2 °C	30.0 psi @Temperature 72.0 °F	Lap Shear Unprimed, 12 months at 300°F
	16.0 MPa @Temperature 149 °C	2320 psi @Temperature 300 °F	Lap Shear
	22.99 MPa @Temperature 149 °C	3335 psi @Temperature 300 °F	Lap Shear Unprimed, No conditioning of Redux 319
	22.99 MPa @Temperature 149 °C	3335 psi @Temperature 300 °F	Lap Shear Primed, No conditioning of Redux 319
	38.0 MPa @Temperature 22.2 °C	5510 psi @Temperature 72.0 °F	Lap Shear, Primed with Redux 119
	42.0 MPa @Temperature 22.2 °C	6090 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in water/methanol at 72°F
	42.0 MPa @Temperature 22.2 °C	6090 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in Skydrol 500A at 72°F
	42.0 MPa @Temperature 22.2 °C	6090 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in distilled water at 72°F
	42.99 MPa @Temperature 22.2 °C	6235 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in Silcodyne 'H' at 72°F
	42.99 MPa @Temperature 22.2 °C	6235 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in distilled water at 72°F
	42.99 MPa @Temperature 22.2 °C	6235 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in water/methanol at 72°F
	42.99 MPa @Temperature 22.2 °C	6235 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in hydraulic oil at 72°F
	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in Skydrol 500A at 72°F
	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, No conditioning of Redux 319
	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in synthetic esters at 72°F
	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in synthetic esters at 72°F
	44.0 MPa @Temperature 22.2 °C	6380 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in anti-icing fluid at 72°F
	44.99 MPa @Temperature 22.2 °C	6525 psi @Temperature 72.0 °F	Lap Shear Unprimed, 1000 hrs in Kerosene fuel at 72°F
	44.99 MPa @Temperature 22.2 °C	6525 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in Kerosene fuel at 72°F
	44.99 MPa @Temperature 22.2 °C	6525 psi @Temperature 72.0 °F	Lap Shear Primed, No conditioning of Redux 319
	44.99 MPa @Temperature 22.2 °C	6525 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in Silcodyne 'H' at 72°F
	46.0 MPa @Temperature 22.2 °C	6670 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in anti-icing fluid at 72°F
	46.0 MPa @Temperature 22.2 °C	6670 psi @Temperature 72.0 °F	Lap Shear Primed, 1000 hrs in hydraulic oil at 72°F
Peel Strength	6.68 kN/m @Temperature 22.2 °C	38.1 pli @Temperature 72.0 °F	Bell Peel
	6.87 kN/m @Temperature 22.2 °C	39.2 pli @Temperature 72.0 °F	Bell Peel, Primed with Redux 119

Processing Properties	Metric	English	Comments
Shelf Life	18.0 Month @Temperature -17.8 °C	18.0 Month @Temperature 0.000 °F

Descriptive Properties	Value	Comments
Areal Weight (psf)	0.08
Climbing Drum Peel (in-lb/3in)	103.2	72°F
	107.7	Primed with Redux 119; 72°F
Standard Roll (ft2)	430
Support	Woven nylon carrier