LG Chemical LUPOY EF1006F PC, Halogen Free, Flame Retardant, High Heat Resistance

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY EF1006F PC, Halogen Free, Flame Retardant, High Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardant, High Heat ResistanceApplication: IT/OA Housing and Components (Adaptor)CAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0070 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 12 g/10 min
<br>@Load 1.20 kg,<br> Temperature 300 °C
 12 g/10 min
<br>@Load 2.65 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength, Yield 61.8 MPa
<br>@Thickness 3.20 mm
 8960 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %
<br>@Thickness 3.20 mm
 >= 100 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 95.1 MPa
<br>@Thickness 3.20 mm
 13800 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.26 GPa
<br>@Thickness 3.20 mm
 327 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 7.55 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 >= 14.1 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
<br>@Thickness 6.40 mm
 266 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 140 °C
<br>@Load 5.00 kg
 284 °F
<br>@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 80.0 °C
<br>@Thickness >=1.00 mm
 176 °F
<br>@Thickness >=0.0394 in
120 °C
<br>@Thickness >=1.50 mm
 248 °F
<br>@Thickness >=0.0591 in
120 °C
<br>@Thickness >=1.70 mm
 248 °F
<br>@Thickness >=0.0669 in
125 °C
<br>@Thickness >=3.00 mm
 257 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C
<br>@Thickness >=1.00 mm
 176 °F
<br>@Thickness >=0.0394 in
115 °C
<br>@Thickness >=1.50 mm
 239 °F
<br>@Thickness >=0.0591 in
115 °C
<br>@Thickness >=1.70 mm
 239 °F
<br>@Thickness >=0.0669 in
120 °C
<br>@Thickness >=3.00 mm
 248 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C
<br>@Thickness >=1.00 mm
 176 °F
<br>@Thickness >=0.0394 in
120 °C
<br>@Thickness >=1.50 mm
 248 °F
<br>@Thickness >=0.0591 in
120 °C
<br>@Thickness >=1.70 mm
 248 °F
<br>@Thickness >=0.0669 in
125 °C
<br>@Thickness >=3.00 mm
 257 °F
<br>@Thickness >=0.118 in
Flammability, UL94 V-0
<br>@Thickness >=1.00 mm
 V-0
<br>@Thickness >=0.0394 in
V-0
<br>@Thickness >=1.50 mm
 V-0
<br>@Thickness >=0.0591 in
V-0
<br>@Thickness >=1.70 mm
 V-0
<br>@Thickness >=0.0669 in
V-0
<br>@Thickness >=3.00 mm
 V-0
<br>@Thickness >=0.118 in
5VB
<br>@Thickness >=3.00 mm
 5VB
<br>@Thickness >=0.118 in
5VA
<br>@Thickness >=1.70 mm
 5VA
<br>@Thickness >=0.0669 in
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Middle Barrel Temperature 280 - 300 °C
536 - 572 °F
Injection Molding
Front Barrel Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Nozzle Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Melt Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding