Stratasys® Polycarbonate
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Stratasys |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stratasys® Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating strong parts that withstand functional testing. It also has superior mechanical properties to ABS and a number of other thermoplastics. When combined with Stratasys FDM (Fused Deposition Modeling) systems, PC gives you Real Parts™ for producing design verification prototypes and manufacturing end-use parts.Information provided by Stratasys®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | Type 1, 2"/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | Type 1, 2"/min; ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.137 GPa | 309.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.5339 J/cm | 1.000 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.6695 J/cm | 5.0011 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 68.4 µm/m-°C @Temperature 20.0 °C |
38.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| Glass Transition Temp, Tg | 161 °C | 322 °F | DSC (SSYS) |
| Flammability, UL94 | V-2 @Thickness 1.10 mm |
V-2 @Thickness 0.0433 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.96 @Frequency 1.00e+6 Hz |
2.96 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.17 @Frequency 60.0 Hz |
3.17 @Frequency 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60112 |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 6019
- Nilit FRIANYL C73 H-GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced
- Teknor Apex Telcar® TL-4145A Thermoplastic Elastomer
- A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
- Tra-Con Tra-Cast 3143 Fire Retardant Epoxy Casting Compound
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling
- Covestro Makrolon® 3152 Polycarbonate
- ChevronTexaco SUPREME Antifreeze/Coolant, Concentrate
- Borealis MB350WG Polypropylene Compound, Mineral Filled
- Resinlab® SEC1222 Silver Filled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved