LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUPOS
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0030 cm/cm
<br>@Thickness 3.20 mm
 0.0020 - 0.0030 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 3.5 g/10 min
<br>@Load 3.80 kg,<br> Temperature 230 °C
 3.5 g/10 min
<br>@Load 8.38 lb,<br> Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength, Yield 98.1 MPa
<br>@Thickness 3.20 mm
 14200 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 4.0 %
<br>@Thickness 3.20 mm
 4.0 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 118 MPa
<br>@Thickness 3.20 mm
 17100 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 4.90 GPa
<br>@Thickness 3.20 mm
 711 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 1.10 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
<br>@Thickness 6.40 mm
 216 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
Flammability, UL94 V-0
<br>@Thickness >=1.50 mm
 V-0
<br>@Thickness >=0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 235 °C
428 - 455 °F
Injection Molding
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Front Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Nozzle Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Melt Temperature 235 - 245 °C
455 - 473 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 80 rpm
40 - 80 rpm
Injection Molding