SABIC Innovative Plastics LNP THERMOCOMP UF00BAS PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF00BAS PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* UF00BAS is a compound based on Polyphthalamide containing 55% Glass Fiber. Added feature of this material is: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | ASTM D792 |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 227 MPa | 32900 psi | 5 mm/min; ISO 527 |
| 246 MPa | 35700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 18.87 GPa | 2737 ksi | 1 mm/min; ISO 527 |
| 19.24 GPa | 2791 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 314 MPa | 45500 psi | ISO 178 |
| 338 MPa | 49000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 15.91 GPa | 2308 ksi | 2 mm/min; ISO 178 |
| 17.3 GPa | 2510 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.91 J/cm | 5.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 28.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 293 °C | 559 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 289 °C @Thickness 3.20 mm |
552 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 272 °C | 522 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 270 °C @Thickness 3.20 mm |
518 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products T10UP100-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black, UL94 HB Rated
- Solvay Specialty Polymers Halar® 350LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)&
- Solvay Specialty Polymers Tecnoflon® PL 455 Fluoroelastomer
- SABIC Innovative Plastics LNP THERMOCOMP D451 PC (Asia Pacific)
- SK Chemicals SKYTHANE® 185A R series Polyurethane
- Samyang Tramid® 210P Polyamide, High Productivity
- Assab Steels 709M Machinery Steel
- A. Schulman ComAlloy Comtuf® 604 Nylon 6/6, Impact Modified, Flow Enhanced
- A. Schulman ComAlloy Comtuf® 524 Polycarbonate/Styrenic Alloy
- LATI Latilub 80-17ST G/30 PPS, 30% Glass Fiber Reinforced, Silicone/PTFE Filled