Polymer Property : Linear Mold Shrinkage, Flow = 0.0030 in/in Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955
PolyOne LubriOne™ NN-30GF/15T Black Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	ASTM D955
PolyOne Maxxam™ MX5210-0040 RS Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955
PolyOne Trilliant™ HC HC6600-0010 ESD Black Polyamide 66 (Nylon 66) Information provided by PolyOne
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	ASTM D955
Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in
Idemitsu Kosan XarecÂ® WA 214LG SPS, 40% Glass Filled Crystalline Polymer, Glass Filled
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0020 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1510 compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RCL26 PA6.6 LNP* LUBRICOMP* RCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	on tensile bar; SABIC Method
SABIC Innovative Plastics LNP Lubricomp RCP36XXQ PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RCP36XXQ is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Easy Molding, Internally Lu..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UFL36SXP is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Heat Stabilized.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON AX02747 ABS LNP* STAT-KON* AX02747 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.18 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.125 in
Solvay Specialty Polymers AvaSpireÂ® AV-722 SL30 Polyaryletherketone (PAEK) AV-722 SL30 is a wear resistant grade of AvaSpireÂ® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to the outstanding..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.18 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.125 in
Solvay Specialty Polymers AvaSpireÂ® AV-750 GF40 Polyaryletherketone (PAEK), 40% Glass Fiber AvaSpireÂ® AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical ch..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	SABIC Method
SABIC Innovative Plastics LNP STAT-KON DEL329EP PC (Europe-Africa-Middle East) LNP* STATKON* DEL329EP is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features include: Electrically Conductive, Internally Lubricated, Flame retard..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific) LNP* Stat-Kon* DX10315C is carbon fiber filled polycarbonate composite with good stiffness, good flow ability, ESD safety, and high level of cleanliness for the most demanding application. This comp..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	ASTM D955
Shinkong Synthetic Fibers ShiniteÂ® T102G30 PET, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP D351 PC (Asia Pacific) LNP* Thermocomp* D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus,..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP EXTC8143 PC (Asia Pacific) LNP* Thermocomp* EXTC8143 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, No..
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0020 - 0.0030 in/in <br>@Thickness 0.126 in	ASTM D955
Samsung Cheil Industries InfinoÂ® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Time 86400 sec	0.0010 - 0.0030 in/in <br>@Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber.
Linear Mold Shrinkage, Flow	0.0026 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0026 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL IGN320 PPE+PS 20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils.
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0020 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL PX2956 PPE+PS (Asia Pacific) PPE+PS GF+Mineral Filler total 35% FR V-0
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	SABIC Method
SABIC Innovative Plastics LNP STAT-KON DX05042 PC (Europe-Africa-Middle East) LNP* Stat-kon* DX05042 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP..
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0020 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics NORYL EM7304F PPE+PS 15% glass reinforced, high flow with enhanced polyurethane foam adhesion for instrument panel retainers.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	ASTM D955
Chase Plastics CP Pryme® PC320R Polycarbonate, Recycled Content Features: Good mold releaseRecycled contentForm: PelletsInformation provided by Chase Plastics.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 4.00 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.157 in	E2P method
Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXA is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm <br>@Thickness 3.20 mm	0.0010 - 0.0030 in/in <br>@Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.