Dow Nordel® IP 4770R General Purpose Compound
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Dow Chemical |
| Trade Name | Nordel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Nordel® IP 4770R General Purpose Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationNordel® IP 4770R
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.083 g/cc | 0.03913 lb/in³ | |
| Mooney Viscosity | 62 @Temperature 100 °C |
62 @Temperature 212 °F |
ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 480 % | 480 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00780 GPa | 1.13 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.0110 GPa | 1.60 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 39.3 kN/m | 224 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 61 % @Temperature 125 °C |
61 % @Temperature 257 °F |
Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -23.0 °C | -9.40 °F | Temperature Retraction, TR-10 |
Users viewing this material also viewed the following:
- Nihon Superior SN100C3 High Temperature Dipper and Tinning Solder
- Humiseal 1B73 Acrylic Conformal Coating
- International Mold Steel TOOLOX 33 Cold Work Die Steel
- SolVin 372NF Polyvinyl Chloride Low Viscosity Paste
- Teknor Apex Sarlink® 3440 Thermoplastic Elastomer
- DuPont™ Nomex® E56 Paper, 20 mil Nominal Thickness
- Huntsman Rexell® L2101 Injection Molding LLDPE (discontinued **)
- Beijing Chemical Industry KAIFA® MN-401 PA6 Resin
- Solvay RHODICARE S Xanthan Gum Surfactant
Copyright © lookpolymers.com All Rights Reserved