LG Chemical AF305HT ABS, Flame Retardant, Heat Resistance

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical AF305HT ABS, Flame Retardant, Heat Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Flame Retardant, Heat ResistanceApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 9001-96-2, 68928-70-1, and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength, Yield 39.2 MPa

@Thickness 3.20 mm
 5690 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Tensile Modulus 1.96 GPa

@Thickness 3.20 mm
 284 ksi

@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 66.7 MPa

@Thickness 6.40 mm
 9670 psi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 2.26 GPa

@Thickness 6.40 mm
 327 ksi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 0.883 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.77 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 3.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.392 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 0.735 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.588 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.10 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 102 °C

@Thickness 6.40 mm
 216 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C

@Thickness 6.40 mm
 196 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 100 °C

@Load 5.00 kg
 212 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 85.0 °C

@Thickness >=1.50 mm
 185 °F

@Thickness >=0.0591 in
 UL 746B
85.0 °C

@Thickness >=2.00 mm
 185 °F

@Thickness >=0.0787 in
85.0 °C

@Thickness >=3.00 mm
 185 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 85.0 °C

@Thickness >=1.50 mm
 185 °F

@Thickness >=0.0591 in
 UL 746B
85.0 °C

@Thickness >=2.00 mm
 185 °F

@Thickness >=0.0787 in
85.0 °C

@Thickness >=3.00 mm
 185 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 85.0 °C

@Thickness >=1.50 mm
 185 °F

@Thickness >=0.0591 in
 UL 746B
85.0 °C

@Thickness >=2.00 mm
 185 °F

@Thickness >=0.0787 in
85.0 °C

@Thickness >=3.00 mm
 185 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
 V-0

@Thickness >=0.0787 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Dielectric Strength 23.0 kV/mm
584 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=2.00 mm
 15 - 30 sec

@Thickness >=0.0787 in
30 - 60 sec

@Thickness >=3.00 mm
 30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 1.50 mm
 60 - 120 arcs

@Thickness 0.0591 in
60 - 120 arcs

@Thickness 2.00 mm
 60 - 120 arcs

@Thickness 0.0787 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 0.490 - 0.981 MPa
71.1 - 142 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding