- Fiberfil® J-69/20/E High performance polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
Fiberfil® J-69/20/E High performance polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-69/20/E High performance polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0040 cm/cm @Thickness 6.35 mm |
0.0040 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 12 g/10 min | 12 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 - 110 | 105 - 110 | ASTM D785 |
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | ASTM D638 |
| Flexural Strength | 101 MPa | 14600 psi | ASTM D790 |
| Flexural Modulus | 4.27 GPa | 620 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 221 °C | 400 - 430 °F | |
| Middle Barrel Temperature | 216 - 232 °C | 420 - 450 °F | |
| Front Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Nozzle Temperature | 204 - 221 °C | 400 - 430 °F | |
| Melt Temperature | 210 - 232 °C | 410 - 450 °F | |
| Mold Temperature | 37.8 - 65.6 °C | 100 - 150 °F | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 BT SD PA66
- Mo-Sci Corporation GB-40-I Green B Filter Glass
- SSAB Tunnplat Domex® Wear Steel Sheet
- Samsung Cheil Industries Starex® HF-0690M ABS, Unreinforced
- EMS-Grivory Grivory® 2D 25 W 20 HL X black 9992 PA612-I
- CPC - Vycom SANATEC® Sanitary Cutting Boards High Density Polyethylene
- ExxonMobil 424 Mobilmet 400 Series
- Eurotec® Tecomid® NA40 GR30 NL RM PA 6.6 30% glass fiber reinforced, low friction and wear
- Colorite Polymers 9012 Clear Injection Molding Vinyl Compound
- Ascend Performance Materials Vydyne® R540H Nylon 66, 40% Glass Reinforced, DAM
Copyright © lookpolymers.com All Rights Reserved