Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
RheTech Products GC40P101-00 40% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural Applications: Consumer goodsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.18 mm |
320 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Maxxam™ NT-818.G002-1000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
Nilit FRIANYL B63 V2 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, flame retardant.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 3.18 mm |
320 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Maxxam™ FR QD 818.Y001 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
Nilit FRIANYL B63 E Raw extruded nylon 6 for injection molding Raw extruded nylon 6 for injection molding (available only in nature).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
Nilit RECONYL B F Recycled nylon 6 for injection molding Recycled nylon 6 for injection molding, highly crystallized (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 - 171 °C | 320 - 340 °F | Average value: 163 °C Grade Count:21 |
Overview of materials for Acetal Copolymer, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Carbon Fiber Filled". Each property range of values reported is minimum and maximum va.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
Covestro Apec® DP 1-9349/5 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Ba.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
LG Chemical LUCEL FW-710F Friction and Wear Resistant POM, PTEE filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
LG Chemical LUCEL N127-02 General Purpose POM, Unreinforced, Externally Lubricated, High Flow LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
LyondellBasell Higlass PF062-4 Polypropylene Homopolymer, 40% Glass Fiber Key Features: high melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, excellent processabilityApplications: appliance parts,.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics Ultem ATX100F PEI (Europe-Africa-Middle East) Higher impact, high flow Polyetherimide blend. ECO Conforming, UL94 HB Listing. US FDA Food Contact Compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA6/6 0249 B Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Barium SulfateFeatures: High Specific GravityInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® POM HO 0167 S1 Availability: North AmericaForms: PelletsFiller/Reinforcement: MetalFeatures: HomopolymerInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® POM HO TL20 BN042 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%)Features: Lubricated and HomopolymerAppearance: Brown, Natural Color and RedInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP Thermotuf R1000IX2 PA6.6 (Europe-Africa-Middle East) LNP* THERMOTUF* R1000IX2 is a compound based on PA 66 resin, containing Impact Modifier. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® POM CO AF15 Availability: North AmericaForms: PelletsAdditive: Aramid Resin Lubricant(15%)Features: Lubricated, Copolymer, Good Wear Resistance and Low FrictionInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Teknor Apex Sinpolene GPP1630 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 30% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
Teknor Apex Sinpolene GPP1640 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 40% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
Washington Penn High Modulus Polypropylene Homopolymer 40% Glass Filled Mica-filled polypropylene compounds provide the best strength and modulus of any of the particulate fillers which results in an outstanding balance of properties. Mold shrinkage is similar to ABS a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | >= 160 °C | >= 320 °F | DIN 53461 |
Polyram PlusTek RB703 Nylon 6, UV Stabilized General purpose, UV stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
Washington Penn Homopolymer Polypropylene 40% Glass Reinforced Fiberglass & mineral-reinforced polypropylene compounds provide excellent tensile and impact properties. Mold shrinkage is similar to ABS and polystyrene. Compounds also have dimensional stability. .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
Polyram RamSter PF702 PBT, UV Stabilized UV stabilized, medium viscosity PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | DIN 53461 |
Polyram RamTal PM7109 Acetal, UV Stabilized UV stabilized polyacetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | >= 160 °C | >= 320 °F | ISO 75; DIN 53461 |
Zell-Metall Engineering Plastics Zellamid 202 (PA 6) Zellamid® 202 is a tough material with high resistance to abrasion and impact. It features good mechanical properties. By water absorption the excellent shock and vibration resistance is increased... |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-2 |
Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound Xmod K65G2 is a 20% glass fiber reinforced grade intended for injection molding. Xmod K65G2 has been developed especially for the car industry, to be used UTB parts. Xmod K65G2 offers good balance.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
Aclo Accutech Polypropylene Homopolymer HP0334G40CL Glass Reinforced Coupled |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
BASF Procom® D 1153 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 -1 & -2 flat |
Asahi Kasei Tenac®-C HC450 Copolymer Acetal Resin New Copolymer, the improvement of physical properties of standard gradesInformation provided by Asahi Kasei Corporation. |