SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RFD02 is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ISO 294 |
| 0.014 - 0.016 cm/cm @Time 86400 sec |
0.014 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
| 77.0 MPa | 11200 psi | ASTM D638 | |
| Elongation at Break | 5.1 % | 5.1 % | ISO 527 |
| 5.5 % | 5.5 % | ASTM D638 | |
| Tensile Modulus | 7.40 GPa | 1070 ksi | 1 mm/min; ISO 527 |
| 8.27 GPa | 1200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| 139 MPa | 20200 psi | ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 6.30 GPa | 914 ksi | ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.13 J/cm | 3.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 48.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 236 °C @Thickness 3.20 mm |
457 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL4419 PC Copolymer (Europe-Africa-Middle East)
- Plaslok 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **)
- A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6
- A. Schulman POLYBATCH™ White LL8844 GP
- Eastman Tenite 360E4861314 Cellulose Acetate Propionate, Clear, Trsp
- Fainplast Compounds Hax™ HF 039/4H Flame Retardant Polyolefin Cable Compound
- Colorite Polymers 9273E General Purpose Vinyl Compound
- Braskem D040A Homopolymer Polypropylene
- 3M Nextel™ 610 Composite Ceramic Fiber
- ATI Allvac® Nickelvac® HC-276 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) Anneal
Copyright © lookpolymers.com All Rights Reserved