Kolon KOPA® KN133G50 G/F Reinforced Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN133G50 G/F Reinforced Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubrication and abrasion resistance, excellent chemical resistance, wide usage temperature, good impact absorbing characteristicsInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 206 MPa | 29900 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 333 MPa | 48400 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm | 3.31 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 220 °C | 428 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with Sundex 790 Plasticizer
- LyondellBasell Alathon® M5040 High Density Polyethylene
- FKuR Kunststoff Biograde® C 9550 Biodegradable Plastic Compound
- IRPC Polimaxx Polene 2311NCX TA4 Polypropylene Compound
- Styron DL 242NA Functionalized SB
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
- Dow DOWLEX™ 2045.11G Linear Low Density Polyethylene
- 3M 9497 Splicing Tapes
- Asahi Glass Fluon® PB2015 15% Graphite, PTFE Filled Compound
- Ineos Nova 1301 High Heat Crystal Polystyrene
Copyright © lookpolymers.com All Rights Reserved