Clariant 6008 L Nylon 6, High Impact, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant 6008 L Nylon 6, High Impact, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Yield | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm @Temperature 22.8 °C |
17.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 212 °C | 410 - 413 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 °C | 100 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Middle Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Front Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Nozzle Temperature | 254 - 274 °C | 490 - 525 °F | |
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |
| Mold Temperature | 51.7 - 79.4 °C | 125 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.14 - 6.21 MPa | 600 - 900 psi | Secondary |
| 6.89 - 10.3 MPa | 1000 - 1500 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Shakespeare Isocorâ„¢ SVP4011 high viscosity PA-6/69
- SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East)
- A. Schulman FORMION™ FI 395 Ionomer
- Cossa Polimeri ESTAPROP H 0560 HFC Polypropylene, 30% Glass Filled
- Covestro Makrolon® 3103 Polycarbonate
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 8% Plasticizer (discontinued **)
- LNP Thermocomp® OF-1008 Polyphenylene Sulfide, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved