E-Polymers SEPAZ® LH60 PP Homopolymer LFT Resin

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	E-Polymers Co. Ltd.
Trade Name	SEPAZ®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers SEPAZ® LH60 PP Homopolymer LFT Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and delivers optimal reinforcement to the plastic matrix in contrast to conventional short glass fiber-reinforced thermoplastics. Molded parts made of SEPAZ LFT are used in virtually every sector of consumer and industrial manufacturing, including automotive, recreation & sports, marine, food & beverage.Information Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ASTM D792
Water Absorption	0.020 % @Time 86400 sec	0.020 % @Time 24.0 hour
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	137.34 MPa	19920 psi	ASTM D638
Elongation at Break	1.5 %	1.5 %	ASTM D638
Flexural Strength	215.82 MPa	31302 psi	ASTM D790
Flexural Modulus	12.26 GPa	1779 ksi	ASTM D790
Izod Impact, Notched	2.65 J/cm @Temperature 23.0 °C	4.96 ft-lb/in @Temperature 73.4 °F	ASTM D256
	2.65 J/cm @Temperature -30.0 °C	4.96 ft-lb/in @Temperature -22.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	165 °C	329 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 230 °C	428 - 446 °F
Mold Temperature	40.0 - 70.0 °C	104 - 158 °F