A. Schulman POLYFORT™ FPP 1080 Glass Fiber-Reinforced Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1080 Glass Fiber-Reinforced Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1080 is a 20% fiber-reinforced homopolymer polypropylene with excellent strength and heat resistance. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 5.0 g/10 min @Temperature 230 °C |
5.0 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.720 J/cm | 1.35 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.85 J/cm | 3.47 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC F04660 High Density Polyethylene for Blown Film Applications
- Multibase Multi-Pro® 5002 X White 50% Filler Content Polypropylene
- 3M Dyneon™ PFA 6502N Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Kaiser 7068 T6, T6511 Rod & Bar
- SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer (Europe-Africa-Middle East)
- ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin
- Ascend Performance Materials Vydyne® 22HSP NT Nylon 66, Conditioned
- Ashley Polymers Ashlene® 257 PPO
Copyright © lookpolymers.com All Rights Reserved