Multibase Nylex™ 2185 R30 Polyamide + PP
| Category | Polymer , Thermoplastic , Nylon , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Nylex™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Nylex™ 2185 R30 Polyamide + PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforcement, 30% Filler by Weight Features: Crack Resistance, GoodDimensional Stability, GoodImpact Resistance, GoodMoisture ResistantProcessability, GoodForms:PelletsProcessing Methods:Injection MoldingUses: Electrical PartsHousing, Electrical Safety EquipmentInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM 792 |
| Water Absorption | 0.65 % | 0.65 % | ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 0.71 g/10 min | 0.71 g/10 min | Cond. Q; ASTM D1238 |
| 2.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 54.3 MPa | 7870 psi | ASTM D638 |
| Elongation at Break | 23 % | 23 % | ASTM D638 |
| Flexural Strength | 75.2 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 4.21 GPa | 611 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 1.356 J | 1.000 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 205 °C | 401 °F | |
| Middle Barrel Temperature | 208 °C | 406 °F | |
| Front Barrel Temperature | 213 °C | 415 °F | |
| Nozzle Temperature | 213 °C | 415 °F | |
| Mold Temperature | 13.0 - 47.8 °C | 55.4 - 118 °F | |
| Injection Pressure | 2.41 - 8.27 MPa | 350 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Moderate-Fast |
Users viewing this material also viewed the following:
- MV Labs PR810 Pr6O11 Praseodymium(III),IV) oxide
- PPT LSF180 Low Sintering Temperature Ferrite Powder
- Ineos H03W-01 Polypropylene, Gas Phase Polymerized
- SABIC Innovative Plastics LNP THERMOCOMP KF006 Acetal Copoly
- Solvay TECHNYL® A 218 V35 Black 34 NG PA66, 35% glass fiber, Conditioned
- Covestro Makrolon® 6585 Polycarbonate, Flame Retardant Grade
- Chosun Refractories TCH-175S Torpedo Castable
- Arkema Group Rilsan® AMN D Nylon 12, Rigid, Injection Grade (Conditioned)
- DuPont Fusabond® MD226D Linear Low Density Polyethylene (discontinued **)
- Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone
Copyright © lookpolymers.com All Rights Reserved