BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. It is also available in heat stabilized (Ultramid 8331G HI HS) and/or pigmented versions.

Physical Properties	Metric	English	Comments
Density	1.16 g/cc	0.0419 lb/in³	Melt; ISO 1183
	1.34 g/cc	0.0484 lb/in³	ISO 1183
Water Absorption	0.90 %	0.90 %	24 hour; ISO Test
	5.5 %	5.5 %	ISO 62
Moisture Absorption at Equilibrium	1.5 %	1.5 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM Test
Tensile Strength at Break	152 MPa	22000 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	145 MPa	21000 psi	5mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5mm/min; ISO 527
	3.5 %	3.5 %	0.2 in/min; ASTM Test
Tensile Modulus	9.30 GPa	1350 ksi	1mm/min; ISO 527
	2.66 GPa @Temperature 120 °C	386 ksi @Temperature 248 °F	ISO Data
	9.20 GPa @Temperature -40.0 °C	1330 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	215 MPa	31200 psi	ISO Data
	241 MPa	35000 psi	ASTM Test
	89.0 MPa @Temperature 120 °C	12900 psi @Temperature 248 °F	ASTM Test
	105 MPa @Temperature 93.0 °C	15200 psi @Temperature 199 °F	ASTM Test
	130 MPa @Temperature 65.0 °C	18900 psi @Temperature 149 °F	ASTM Test
	310 MPa @Temperature -40.0 °C	45000 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	7.20 GPa	1040 ksi	ISO Data
	8.00 GPa	1160 ksi	ASTM Test
	3.04 GPa @Temperature 120 °C	441 ksi @Temperature 248 °F	ASTM Test
	3.28 GPa @Temperature 93.0 °C	476 ksi @Temperature 199 °F	ASTM Test
	4.04 GPa @Temperature 65.0 °C	586 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	2.39 J/cm @Thickness 3.17 mm	4.48 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	21.0 kJ/m²	9.99 ft-lb/in²	ISO Test
	14.0 kJ/m² @Temperature -40.0 °C	6.66 ft-lb/in² @Temperature -40.0 °F	ISO Test
Charpy Impact Unnotched	7.80 J/cm²	37.1 ft-lb/in²	ISO 179
Charpy Impact, Notched	2.00 J/cm²	9.52 ft-lb/in²	ISO 179
	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	24.0 µm/m-°C	13.3 µin/in-°F	ISO 11359
CTE, linear, Transverse to Flow	84.0 µm/m-°C	46.7 µin/in-°F	ISO 11359
Specific Heat Capacity	1.958 J/g-°C	0.4680 BTU/lb-°F	Melt
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	Melt
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	205 °C	401 °F	ISO 75
	210 °C	410 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz	3.4 @Frequency 1.00e+6 Hz	IEC 60250
	3.6 @Frequency 100 Hz	3.6 @Frequency 100 Hz	IEC 60250
	3.8 @Frequency 1e+9 Hz	3.8 @Frequency 1e+9 Hz	ASTM Data
	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	ASTM Data
Dielectric Strength	43.0 kV/mm	1090 kV/in	IEC 60243-1
Dissipation Factor	0.010 @Frequency 1e+9 Hz	0.010 @Frequency 1e+9 Hz	ASTM Data
	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	ASTM Data
	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	IEC 60250
	0.010 @Frequency 100 Hz	0.010 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes