Polymer Property : Flexural Strength = 18900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	130 MPa	18900 psi
Plastcom SLOVASTER® B1 GF 10 PBT, 10% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 10% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending..
Flexural Strength	130 MPa	18900 psi	ISO 178
Nilit FRIANYL A63 HS-GV25 Nylon 6.6 for injection molding, 25% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	130 MPa	18900 psi
Pyrotek TS-117 Thermoset Electrical Insulation Product (Nema Grade: GPO-1) Glass reinforcement, Polyester resin, Gray color. Economical, general purpose product.Information provided by Pyrotek.
Flexural Strength	130 - 150 MPa	18900 - 21800 psi	Injection; ISO 178
Raschig Group 2557 AMC Polyester Glass fiber reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, exceptional processability with short cycle time and low ..
Flexural Strength	130 MPa @Temperature 23.0 °C	18900 psi @Temperature 73.4 °F	DAM; ISO 178
DuPont Performance Polymers Zytel® HTN 52GM50EF WT001 Polyphthalamide (PPA) (Unverified Data**) Zytel® HTN52GM50EF WT001 is a glass and mineral reinforced high performance polyamide resin developed for LED reflector applications. It is also a PPA resin.Information provided by DuPont Performan..
Flexural Strength	130 MPa	18900 psi
Plastcom SLOVAMID 6 GF 5 PA6, 5% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 5% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and ..
Flexural Strength	<= 130 MPa	<= 18900 psi	ISO 178
Polykemi AB POLYfill PPH GF10030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB
Flexural Strength	130 MPa	18900 psi
Lehmann & Voss LUVOCOMÂ® 1105-7741 PEEK, with mineral filler, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,..
Flexural Strength	130 MPa	18900 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Asia Pacific) LNP* Lubricomp* KFL36 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	130 MPa	18900 psi	ISO 178
SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Strength	130 MPa	18900 psi	ISO 178
Solvay Specialty Polymers RytonÂ® QC160N Polyphenylene Sulfide (PPS) RytonÂ® QC160N (granular powder) unfilled polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and is suitable for thermoplastic extrusion processes.Features: Good Ch..
Flexural Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® VX5011 PBT (Europe-Africa-Middle East) VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics.
Flexural Strength	130 MPa	18900 psi	ISO 178
SABIC Innovative Plastics LNP Thermocomp EB004 PEI LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	130 MPa	18900 psi	ASTM D790
SABIC Innovative Plastics NORYL NF2020 PPE+PS (Asia Pacific)
Flexural Strength	130 MPa	18900 psi	DIN 54352
Schwartz Technical Plastics OPTAMIDÂ® Cast Polyamide 6, Dry Application: deflection rope sheaves for elevatorsInformation provided by Schwartz Technical Plastics GmbH
Flexural Strength	130 MPa	18900 psi	ASTM D790
Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant 25% glass beads and glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	130 MPa	18900 psi	ISO 178-93
Wellman Wellamid® MR410 22H-WBK 40% Mineral Reinforced, Weatherable Black Nylon 66 Description: Mineral Reinforced, Weatherable Black Nylon 66Information provided by Wellman.
Flexural Strength	130 MPa	18900 psi	ASTM D790
Polyram RamTough RZ300G3 Polycarbonate, 15% Glass Fiber 15% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	130 MPa @Thickness >=1.50 mm	18900 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Reinforced with a finer cotton fabric than Etronax MF. Also well suited in particular for small components which are subject to mechanical load and wear. Can be machined to finer tolera..
Flexural Strength	130 MPa @Thickness >=1.50 mm	18900 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola Etronax MMMF PTFE Phenolic, Cotton Fabric Reinforcement, Light Brown, Sheets Description: Friction reducing material consisting of phenolic resin with PTFE (Teflon®) and a very fine cotton fabric. Exclusively for mechanical applications. Very good dry run properties. Well s..
Flexural Strength	130 - 140 MPa	18900 - 20300 psi	ASTM D790, ISO 178
EPICHEM Epilon G4-PC 20% GF Polycarbonate, 20% Glass Fiber Characteristics: 20% glass fibre filled, excellent mechanical properties
Flexural Strength	130 MPa	18900 psi	DAM; ISO 178
DuPont Performance Polymers Zytel® HTN 52GM50EF WT001 Polyphthalamide (PPA) (Unverified Data**) 50% Glass/Mineral Reinforced PPA High Performance Polyamide Zytel HTN52GM50EF WT001 is a glass and mineral reinforced high performance polyamide resin developed for LED reflector applications. It is..
Flexural Strength	130 MPa	18900 psi	ISO Data
BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS BK-102 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and d..
Flexural Strength	130 MPa @Temperature 65.0 °C	18900 psi @Temperature 149 °F	ASTM Test
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of st..
Flexural Strength	130 MPa	18900 psi	at max force; ISO 178
BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Dry) Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and ele..