SABIC Innovative Plastics LNP Thermocomp PFB42EU PA 6 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp PFB42EU PA 6 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* PFB42EU is a compound based on PA 6 resin containing Glass Fiber, Glass Bead. Added features include Easy Molding, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	ISO 1183
Water Absorption	1.9 % @Temperature 23.0 °C, Time 86400 sec	1.9 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.0044 cm/cm	0.0044 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	93.0 MPa	13500 psi	5 mm/min; ISO 527
Elongation at Break	2.6 %	2.6 %	5 mm/min; ISO 527
	4.4 %	4.4 %	Flexural Strain, 2 mm/min; ISO 178
Tensile Modulus	5.70 GPa	827 ksi	1 mm/min; ISO 527
Flexural Strength	145 MPa	21000 psi	2 mm/min; ISO 178
Flexural Yield Strength	145 MPa	21000 psi	2 mm/min; ISO 178
Flexural Modulus	4.70 GPa	682 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	20.0 kJ/m² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	49.0 µm/m-°C @Temperature 23.0 - 60.0 °C	27.2 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	93.0 µm/m-°C @Temperature 23.0 - 60.0 °C	51.7 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	156 °C	313 °F	Flatw 80104 sp=64mm; ISO 75/Af

Users viewing this material also viewed the following: