Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 130 MPa | 18900 psi | STN EN ISO 178 |
Plastcom SLOVAMID 66 W 40 Polyamide 66, 40% Mineral Filled FeaturesPA 66 with the content of 40% chemically modified mineral filler. Used for grips of electric hand tools, hobby tools, gear wheels, covers of electric tools, flat products, automobile wheel .. |
|||
Flexural Strength | 130 MPa | 18900 psi | STN EN ISO 178 |
Plastcom SLOVASTER® B GF 10 Polybutylene Terephthalate, 10% Glass Fiber FeaturesPBT for injection moulding, chemically reinforced with 10% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Nilit FRIANYL A63 HS-GV25 Nylon 6.6 for injection molding, 25% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
DAM; ISO 178 |
DuPont Performance Polymers Zytel® HTN 52GM50EF WT001 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTN52GM50EF WT001 is a glass and mineral reinforced high performance polyamide resin developed for LED reflector applications. It is also a PPA resin.Information provided by DuPont Performan.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 1105-7753/BL PEEK, unreinforced, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 50/CF/7/GS/10/TF/5/EM/BK Polycarbonate, with carbon fiber, glass flakes and PTFE, easy flowing Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 80-7388 Polyacetal-copolymer, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit.. |
|||
Flexural Strength | 130 MPa | 18900 psi | |
Lehmann & Voss LUVOCOM® 80-7555/BK Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KFL25 Acetal Copolymer LNP LUBRICOMP* KFL25 is a compound based on Acetal Copolymer resin containing 25% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Solvay TECHNYL® A 548B V15 PA66, 15% glass fiber, DRY Description: TECHNYL® A 548B V15 is a copolyamide 6.6/6, reinforced with 15% of glass fiber, heat stabilized, impact modified, for blow molding. This product is available in black color.Benefits:.. |
|||
Flexural Strength | 130 MPa | 18900 psi | DIN 54352 |
Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Dry Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS LNP THERMOCOMP* AF004AH is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Healthcare. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp EB004 PEI LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF004 ABS LNP* THERMOCOMP* AF004 is a compound based on ABS resin containing 20% Glass Fiber. |
|||
Flexural Strength | 130 MPa | 18900 psi | Flexural Strain: 0.9%; ISO 178 |
Polyplastics Freqtis® P1210A (PPS/LCP), Molding Compound Both base resins (PPS and LCP) exhibit excellent heat resistance, dimensional stability and molding processability. Therefore Freqtis® is widely used for surface mounted electronic components. In .. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant 25% glass beads and glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178-93 |
Wellman Wellamid® MR410 22H-NBK1 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178-93 |
Wellman Wellamid® MR410 22H-WBK 40% Mineral Reinforced, Weatherable Black Nylon 66 Description: Mineral Reinforced, Weatherable Black Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Polyram Polytron P20B03 Polypropylene, 20% Long Glass Fiber A chemically coupled 20% long glass fibers reinforced black polypropylene, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM F417 |
CoorsTek Porcelain Information provided by CoorsTek. |
|||
Flexural Strength | 130 MPa | 18900 psi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® HTN 52GM50EF WT001 Polyphthalamide (PPA)
(Unverified Data**) 50% Glass/Mineral Reinforced PPA High Performance Polyamide Zytel HTN52GM50EF WT001 is a glass and mineral reinforced high performance polyamide resin developed for LED reflector applications. It is.. |
|||
Flexural Strength | >= 130 MPa | >= 18900 psi | Perpendicular to laminations; IEC 1212-2 5.1 |
Hippe UP GM 202 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet Used in mechanical and electrical applications. Good stability of electrical properties under high humidity. Good mechanical properties at moderate temperature. Flame retardant.Information provid.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
Eurotec® Tecodur® PB70 GR20 NL IH PBT 20% glass fiber reinforced, impact modified Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance.. |
|||
Flexural Strength | 130 MPa | 18900 psi | Transverse direction; ISO 178 |
Azdel Plus U400-B01N 41.5% Directionalized Continuous Fiber Mat / PP Resin Matrix AZDEL® U400-B01N is a uni-directional fiber and random glass mat reinforced polypropylene composite material featuring excellent fiber distribution over long flow paths and complex part forms. Thi.. |
|||
Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
Asahi Kasei Thermylene® P7-30FG-0890 30% Glass Fiber Reinforced, UV Stabilized Information provided by Asahi Thermofil |