- Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant
- Gichem GILAC A50VX35/VO ABS Flame Retardant (discontinued **)
Gichem GILAC A50VX35/VO ABS Flame Retardant (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Glass Fiber Filled, Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gichem GILAC A50VX35/VO ABS Flame Retardant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS self-extinguishing class V0, 17% glass fiber filled, good stiffness. Medium injection speed.Information provided by GICHEM Gruppo Industriale Chimico
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525/A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Flammability Test | 75 | 75 | [°C] Bilia; IEC 331 |
| Oxygen Index | 37 % | 37 % | ASTM D2863 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 2 hours |
Users viewing this material also viewed the following:
- Plenco 5314 Black (COM) Impact Grade Phenolic Molding Compound (discontinued **)
- SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly
- Saint-Gobain CHR® M50 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.004" thick)
- Teknor Apex Sinvicomp SPF 4520 Polyvinyl Chloride, Flexible
- Zircar Zirconia Buster M2-35 Alumina Boards, Discs & Cylinders Insulation
- Dalau Dalcon 021 75% Virgin PTFE, 25% Carbon Coke
- 3M 3W29X Protective UV Tape
- ATI Allvac® Nickelvac® 690 UNS N06690 Nickel Superalloy
- Victrex® Vicote® 705 Polyetheretherketone (PEEK) Powder
Copyright © lookpolymers.com All Rights Reserved