Advanced Polymer Alloys DuraGrip™ DGR 6060 NC Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO)
Manufacturer APA - Advanced Polymer Alloys
Trade Name DuraGrip™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Advanced Polymer Alloys DuraGrip™ DGR 6060 NC Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DuraGrip® DGR 6060NC is designed to be a general purpose Thermoplastic Elastomer (TPE) that is easy to use in injection molding and extrusion processes. DGR 6060NC has an excellent soft touch feel, will bond to olefinics, is easy to color, and is available in FDA compliant formulations. DuraGrip® is not hygroscopic and under normal conditions does not require drying.Information provided by Advanced Polymer Alloys
Physical Properties Metric English Comments
Specific Gravity 0.990 g/cc
0.990 g/cc
ASTM D471; ISO 2781
Viscosity 107000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
107000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
ASTM D3835
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
0.022 cm/cm
0.022 in/in
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
0.015 cm/cm
0.015 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 63
63
Time of 5 seconds; ASTM D2240; ISO 48
Tensile Strength, Ultimate 6.5285 MPa
946.88 psi
After 7 days at 70°C; ASTM D412 ISO 37
6.899 MPa
1001 psi
After 7 days at 100oC; ASTM D412 ISO 37
7.419 MPa
1076 psi
ASTM D412; ISO 37
Elongation at Break 370.44 %
370.44 %
After 7 days at 70°C; ASTM D412 ISO 37
378 %
378 %
ASTM D412; ISO 37
378 %
378 %
After 7 days at 100°C; ASTM D412 ISO 37
Modulus of Elasticity 0.00216 GPa
0.314 ksi
After 7 days at 70°C; ASTM D412 ISO 37
0.00230 GPa
0.334 ksi
After 7 days at 100°C; ASTM D412 ISO 37
100% Modulus 0.00219 GPa
0.318 ksi
ASTM D412; ISO 37
Graves Tear Strength 23.1 kN/m

@Temperature 23.9 °C
132 pli

@Temperature 75.0 °F
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 30
30
Cs-17 Wheel, 1000 g Load; ASTM D3389
Compression Set 23 %
23 %
After 22 Hr at 75°F (24°C); ASTM D395; ISO 815
43 %

@Temperature 70.0 °C
43 %

@Temperature 158 °F
22 hrs.; ASTM D395; ISO 815
71 %

@Temperature 100 °C
71 %

@Temperature 212 °F
22 hrs.; ASTM D395; ISO 815
Tensile Set 11 %
11 %
100% Tension; ASTM D412
Thermal Properties Metric English Comments
Brittleness Temperature -67.2 °C
-89.0 °F
ASTM D746; ISO 812
Processing Properties Metric English Comments
Processing Temperature 204 °C
400 °F
Rear Barrel Temperature 188 - 199 °C
370 - 390 °F
Middle Barrel Temperature 199 - 210 °C
390 - 410 °F
Front Barrel Temperature 216 - 227 °C
420 - 440 °F
Nozzle Temperature 204 - 221 °C
400 - 430 °F
Melt Temperature 199 - 221 °C
390 - 430 °F
Mold Temperature 43.3 - 54.4 °C
110 - 130 °F
Injection Pressure 1.03 - 3.45 MPa
150 - 500 psi
Cycle Time - Injection 0.50 - 2.0 sec
0.50 - 2.0 sec
boost
Screw Speed 25 - 100 rpm
25 - 100 rpm
Cure Time 0.167 - 0.333 min
0.00278 - 0.00556 hour
Cooling Time
Descriptive Properties Value Comments
Fluid Resistance - Volume Change, % (ASTM D471) -13
After 7 Days in Water at 212°F (100°C)
2
After 7 Days in ASTM Oil No.1 at 212°F (100°C)
39
After 7 Days in IRM 903 Oil No.3 at 212°F (100°C)
9
After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C)