Aclo Accutech Polypropylene Copolymer CP0436W30L Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436W30L Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 11 g/10 min | 11 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 22 % | 22 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.099 GPa | 304.5 ksi | ASTM D638 |
| Flexural Strength | 26.0 MPa | 3770 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm | 1.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FLS-2530 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Saint-Gobain CHR® 26020 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Techmer ES Luriblend® PA6/6 TL20 Nylon 66
- Lubrizol Isoplast® 2530 Engineering Thermoplastic Polyurethane Resin for Medical Applications
- Teknor Apex Uniprene® 55A Polyvinyl Chloride, Flexible
- Wellman Wellamid® 42LH-XE-NBK1 Nylon 6, Engineering Grade
- A. Schulman CP814-01 Linear, Low-Density Polyethylene
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- CLAL-MSX NICLAL 42 Copper Alloy
- Teknor Apex APEX® 3601-70 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved