Petroquimica Triunfo Tritheva® TN 2020 EVA Copolymer

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Petroquimica Triunfo
Trade Name Tritheva®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Tritheva® TN 2020 EVA Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Tritheva TN 2020 resin is a Ethylene-Vinyl Acetate copolymer (EVA) developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. The structures produced with TN 2020 and PVdC or PA allow radiation treatment and present low rates of water vapor and oxygen permeation, which together ensure a longer shelf life for the food packed in this film. Since it presents an exceptional weldability, this product meets the requirements for automatic or semi-automatic lines of cutting, welding, and/or packaging (with or without vacuum-packed process). Tritheva TN 2020 resin has excellent performance during the extrusion operation, thermal stability, and a low consumption of energy for its processing, rendering to package production a dimensional uniformity and excellent visual properties with high transparency and gloss that enhance the printing and surface finish of the packaging. This product complies with the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1350, to contact with foodstuff.Applications: Shrinkable packaging for food stuff, such as: cheese, meat, ham, salami and other processed meats. Packaging for frozen products.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.931 g/cc
0.0336 lb/in³
ASTM D1505
Vinyl Acetate Content 8.0 - 9.0 %
8.0 - 9.0 %
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 1.7 - 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.7 - 2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
Tensile Strength at Break 19.0 MPa
2760 psi
ASTM D638
Tensile Strength, Yield 7.00 MPa
1020 psi
ASTM D638
Film Elongation at Break, MD 485 %
485 %
ASTM D882
Film Elongation at Break, TD 725 %
725 %
ASTM D882
Elongation at Break 700 %
700 %
ASTM D638
Secant Modulus, MD 0.0670 GPa
9.72 ksi
5%; ASTM D882
Secant Modulus, TD 0.0640 GPa
9.28 ksi
5%; ASTM D882
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ASTM D882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 100 °C
212 °F
ASTM D3418
Vicat Softening Point 79.0 °C
174 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 1.8 %
1.8 %
ASTM D1003
Gloss 140 %
140 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 135 - 150 °C
275 - 302 °F
Plasticizing Zone
145 - 165 °C
293 - 329 °F
Mixture Zone
Feed Temperature 135 - 140 °C
275 - 284 °F
Adapter Temperature 165 - 185 °C
329 - 365 °F
Blow-up Ratio (BUR) 3.0
3.0
Recommended