Samsung Cheil Industries Infino® WP-1089 PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® WP-1089 PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| 47 g/10 min @Load 10.0 kg, Temperature 250 °C |
47 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 54.4 MPa | 7890 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 88 % | 88 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 75.5 MPa | 11000 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.11 GPa | 306 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
3.67 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 3.92 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
7.35 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 4.41 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
8.27 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 5.88 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
11.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.10 µm/m-°C @Temperature 40.0 - 100 °C |
4.50 µin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow | 8.30 µm/m-°C @Temperature 40.0 - 100 °C |
4.61 µin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7690-9 (Black) Thermoplastic Elastomer (TPE)
- PolyOne FireCon™ CPE 30-11 REV 2 Polyethylene, Chlorinated (CPE)
- NOVA Chemicals Sclair® IG454-A Injection Molded HDPE Resin
- LG Chemical LC170 Polyolefin Elastomer for Polymer Modification
- Intercontinental Polymers 1128 Bicomponent PBT/PET Fiber Type - 1.8 Denier X 3 Inches
- Kraton® G1645 M (SEBS) Linear Triblock Copolymer
- SABIC Innovative Plastics LNP THERMOCOMP WC003 PBT (Europe-Africa-Middle East)
- SABIC Innovative Plastics Valox® EXVX1403 PBT (Asia Pacific)
- Master Bond EP29LP Low Exotherm, Low Viscosity Two Component Epoxy System
- PolyOne Geon™ Vinyl Rigid Extrusion L6256 Polyvinyl Chloride, Rigid (PVC, Rigid)
Copyright © lookpolymers.com All Rights Reserved