Toyobo T-423 Nylon, Mineral-Reinforced
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-423 Nylon, Mineral-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Feature: High heat distortion and good toughness, good surfaceInformation provided by Toyobo Co., Ltd
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.67 % | 0.67 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.00 mm |
0.0040 in/in @Thickness 0.118 in |
|
| Linear Mold Shrinkage, Transverse | 0.0045 cm/cm @Thickness 3.00 mm |
0.0045 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Modulus of Elasticity | 6.90 GPa | 1000 ksi | ASTM D638 |
| Flexural Yield Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Yield Strength | 93.0 MPa | 13500 psi | ASTM D695 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17 wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | unregistered |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 29.0 kV/mm @Thickness 2.00 mm |
737 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 123 sec | 123 sec | ASTM D495 |
Users viewing this material also viewed the following:
- NYCOA 2084 HS PA 6
- Orion Engineered Carbons CORAX® N 339 ASTM Carbon Black
- PolyOne Stat-Tech™ PI-10SS/000 Polyetherimide - 10% Stainless Steel Fiber (discontinued **)
- Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Crystalline (discontinued **)
- Kazanorgsintez PE2NT26-13 High Density Polyethylene Composite
- Huntsman IROGRAN® A 95 K 4977 TPU-High Temperature Performance
- Struktol TR EBS Processing Additive, Dispersant
- Tisan TISLAMID® 66 Impact Modified Nylon 66
- Unitika TERRAMAC TE-7000 Polylactic Acid (PLA)
Copyright © lookpolymers.com All Rights Reserved