Polymer Property : Flexural Yield Strength = 19900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 137 MPa
19900 psi
DIN 53455; ASTM D790
Kolon SPELLOY® KB133G15 PC + PBT Alloy Resin  (discontinued **)
SPELLOY® is a new technology of thermoplastic Polymer alloys developed to provide unique combination of excellent mechanical properties.High impact resistance (at low temperature), good dimensional..
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Quantum Composites QC-2130 Phenolic 25% Glass Fiber SMC  (discontinued **)
QC-2130 is a glass-reinforced sheet molding compound based on a phenolic resin matrix. It exhibits outstanding low flammability characteristics. QC-2130 is recommended for applications such as air..
Flexural Yield Strength 137 MPa

@Thickness 3.20 mm
19900 psi

@Thickness 0.126 in
2.8mm/min; ASTM D790
LG Chemical LUMID HI2152A(W) PA6+GF15%, High Impact
Feature: Injection Molding, PA6+GF15%, High ImpactApplication: Automotive PartsCAS No. 25038-54-4, 9010-79-1 and 65997-17-3Information provided by LG Chemical
Flexural Yield Strength 137 MPa

@Thickness 3.20 mm
19900 psi

@Thickness 0.126 in
2.8mm/min; ASTM D790
LG Chemical LUMID LW4203A(W) PA6+GF/MF20%, Low Warpage
Feature: Injection Molding, PA6+GF/MF20%, Low WarpageApplication: Automotive Parts (Engine Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical
Flexural Yield Strength 137 MPa

@Thickness 3.20 mm
19900 psi

@Thickness 0.126 in
10mm/min; ASTM D790
LG Chemical LUPOY GP5206F PC/ABS+GF20%, Flame Retardance
Description: Injection Molding, PC/ABS+GF20%, Flame Retardance, General PurposeApplication: IT/OA (Housing)CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG..
Flexural Yield Strength 137 MPa
19900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM CRS5001 PEI
Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
Flexural Yield Strength 137 MPa
19900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM CRS5001 PEI (Asia Pacific)
Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
Flexural Yield Strength 137 MPa
19900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM CRS5011 PEI (Asia Pacific)
Transparent, Enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Techmer ES Electrablend® PC SS15 FR BK 15% Stainless Steel Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel Fiber, 15% Filler by WeightFeatures: Electromagnetic Shielding (EMI) and Flame RetardantAppearance: BlackInformation pr..
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Shinkong Synthetic Fibers Shinite® T102G15 PET, 15% Glass Filled, Fire Retardant
Information from Shinkong Synthetic Fibers Corp.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Samyang Tribit® 1500G30K PBT, Reinforced Impact
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1500G30K is a reinforced, impact grade.Appl..
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Samyang Trirex® 3025GNH15 Polycarbonate, Reinforced Flame Retardancy, Non-Halogen
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025GNH15 is a reinforced, flame retardant, non-halogen grade.Applications: LCD Panel ..
Flexural Yield Strength 137 MPa
19900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific)
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Flexural Yield Strength 137 MPa
19900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East)
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Flexural Yield Strength 137 MPa
19900 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WCP36 PBT (Europe-Africa-Middle East)
LNP* LUBRICOMP* WCP36 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber, PTFE, Silicone. Added features include; Internally Lubricated, Electrically Conductive.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
PlastxWorld CEVIAN® S1230 PC/ABS alloy
Glass fiber reinforced PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
PlastxWorld CEVIAN® SKG30 30% GF ABS
Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast..
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
PlastxWorld CEVIAN® VGR30 30% GF ABS
Glass fiber reinforced ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
PlastxWorld CEVIAN®-N GRSJ 20% GF SAN resin
Glass fiber reinforced SAN resin. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Tipco Tipcolene® SEB 300 - 30% Chemically Coupled Glass Fiber Polypropylene Homopolymer with High Heat Stability
30% Chemically Coupled Glass Reinforced PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Toyobo T-423 Nylon, Mineral-Reinforced
Key Feature: High heat distortion and good toughness, good surfaceInformation provided by Toyobo Co., Ltd
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Toyobo T-422T Nylon, Mineral-Reinforced
Key Feature: High heat distortion and good toughnessInformation provided by Toyobo Co., Ltd
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Cheng Yu Plastic NG1150S Nylon 66, 15% Glass Fiber Reinforced
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Cheng Yu Plastic NGC3 Nylon 6, 30% Mineral Reinforced
Flexural Yield Strength 137 MPa
19900 psi
2 mm/min; ISO 178
Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
Starflam PX06010 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Cheng Yu Plastic A703G25 ABS 25% Glass Fiber Reinforced
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Cheng Yu Plastic FR200GV15 Flame Retardant Nylon 66, 15% Glass Fiber
Flexural Yield Strength 137 MPa
19900 psi
ASTM D790
Cheng Yu Plastic FRCV200 Flame Retardant Nylon 66, 30% Mineral Reinforced
Flexural Yield Strength 137 MPa
19900 psi
DIN 53452; ASTM D790
Kolon Kopa® KN173MT40 Nylon 6 Resin
KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c..
Flexural Yield Strength 137 MPa
19900 psi
Phenolic 30%, Graphite fabric 70%
Phenyl silane - C.T.L "37-9X". Graphite fabric - "WCB"