Teijin Panlite® LS-2250 Friction and Abrasion Resistant Polycarbonate Resin

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Teijin
Trade Name Panlite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teijin Panlite® LS-2250 Friction and Abrasion Resistant Polycarbonate Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
It is compounded with fluorine powder to improve friction and abrasion resistance, meeting UL 94 V-2. The friction and abrasion resistance is superior than that of polyamidoacetal, maintaining excellent properties of polycarbonate resin. Also provided are those reinforced with GF and CF.Applications:Mechanical, electric and electronic components that need abrasion and friction resistance.Information provided by Teijin Chemicals Ltd.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Water Absorption 0.17 %
0.17 %
in water, 23°C, 24h; ISO 62
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 4.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
50mm/min; ISO 527
Elongation at Break 110 %
110 %
50mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1mm/min; ISO 527
Flexural Strength 80.0 MPa
11600 psi
2mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
ISO 75
Vicat Softening Point 141 °C
286 °F
50°C/hr, 50N; ISO 306
UL RTI, Electrical 115 °C

@Thickness 1.47 mm
239 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical with Impact 105 °C

@Thickness 1.47 mm
221 °F

@Thickness 0.0579 in
UL 746B
UL RTI, Mechanical without Impact 105 °C

@Thickness 1.47 mm
221 °F

@Thickness 0.0579 in
UL 746B
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60243
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 300 V
300 V
IEC 60112