Hexcel® Redux® 830 Two-Part Epoxy Syntactic Paste Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Hexcel
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® Redux® 830 Two-Part Epoxy Syntactic Paste Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Redux® 830 is a low density, self-extinguishing, syntactic, room temperature curing, two-part, epoxy paste adhesive. Redux® 830 is supplied as a 1.5 working kit.Features: Low density; Self-extinguishing; Excellent compressive strength up to 100°C/212°F; Easy to mix by hand; Non-slump; Room temperature or warm curing; Gap filling; Service temperature up to 100°C/212°F; Easily sandable after 4 hours at 22°C/72°F; Less than 0.5% (w/w) volatiles emitted during cure.Applications: Potting; Edge filler in honeycomb sandwich constructions.
Physical Properties Metric English Comments
Density 0.460 g/cc

@Temperature 25.0 °C
0.0166 lb/in³

@Temperature 77.0 °F
Part B, Uncured; ASTM D1875-69
0.620 g/cc

@Temperature 50.0 °C
0.0224 lb/in³

@Temperature 122 °F
Cure Cycle: 5 hours at 50°C; ASTM D792
0.650 g/cc

@Temperature 22.0 °C
0.0235 lb/in³

@Temperature 71.6 °F
Cure Cycle: 5 days at 22°C; ASTM D792
0.720 g/cc

@Temperature 25.0 °C
0.0260 lb/in³

@Temperature 77.0 °F
Part A, Uncured; ASTM D1875-69
Mechanical Properties Metric English Comments
Hardness, Shore D 74

@Temperature -5.56 °C
74

@Temperature 22.0 °F
Dry, Cure Cycle: 5 hours at 50°C
75

@Temperature -5.56 °C
75

@Temperature 22.0 °F
Dry, Cure Cycle: 5 days at 22°C
Compressive Yield Strength 10.0 MPa

@Temperature 100 °C
1450 psi

@Temperature 212 °F
Dry, Cure cycle: 5 hours at 50°C; ASTM D695
16.0 MPa

@Temperature 100 °C
2320 psi

@Temperature 212 °F
Dry,Cure cycle: 5 days at 22°C; ASTM D695
18.0 MPa

@Temperature 60.0 °C
2610 psi

@Temperature 140 °F
Dry,Cure cycle: 5 days at 22°C; ASTM D695
19.0 MPa

@Temperature 80.0 °C
2760 psi

@Temperature 176 °F
Dry,Cure cycle: 5 days at 22°C; ASTM D695
19.0 MPa

@Temperature 80.0 °C
2760 psi

@Temperature 176 °F
Dry, Cure cycle: 5 hours at 50°C; ASTM D695
28.0 MPa

@Temperature 60.0 °C
4060 psi

@Temperature 140 °F
Dry, Cure cycle: 5 hours at 50°C; ASTM D695
38.0 MPa

@Temperature 22.0 °C
5510 psi

@Temperature 71.6 °F
Dry, Cure cycle: 5 hours at 50°C; ASTM D695
44.0 MPa

@Temperature 22.0 °C
6380 psi

@Temperature 71.6 °F
Dry,Cure cycle: 5 days at 22°C; ASTM D695
Compressive Modulus 1.50 GPa

@Temperature 22.0 °C
218 ksi

@Temperature 71.6 °F
Dry, Cure cycle: 5 hours at 50°C; ASTM D695
1.90 GPa

@Temperature 22.0 °C
276 ksi

@Temperature 71.6 °F
Dry, Cure cycle: 5 days at 22°C; ASTM D695
Shear Strength 9.00 MPa

@Temperature 22.0 °C
1310 psi

@Temperature 71.6 °F
Tensile Lap Shear, Dry, Cure cycle: 5 days at 22°C; EN2243-1
10.0 MPa

@Temperature 22.0 °C
1450 psi

@Temperature 71.6 °F
Tensile Lap Shear, Dry, Cure cycle: 5 hours at 50°C; EN2243-1
Processing Properties Metric English Comments
Pot Life 70 min

@Temperature 25.0 °C
70 min

@Temperature 77.0 °F
Mixed, 100g; ASTM 2471 water bath
Gel Time 15.0 - 20.0 min

@Temperature 50.0 °C
15.0 - 20.0 min

@Temperature 122 °F
70.0 - 90.0 min

@Temperature 22.0 °C
70.0 - 90.0 min

@Temperature 71.6 °F
Shelf Life 12.0 Month

@Temperature 5.00 - 27.0 °C
12.0 Month

@Temperature 41.0 - 80.6 °F
Descriptive Properties Value Comments
Burn Length (mm) 13
BSS7230 Method F4; Flammability Horizontal Direction, 15 Second Ignition, Cure cycle: 5 hours at 50°C
19
BSS7230 Method F4; Flammability Horizontal Direction, 15 Second Ignition, Cure cycle: 5 days at 22°C
57
BSS7230 Method F2; Flammability Vertical Direction, 12 Second Ignition, Cure cycle: 5 hours at 50°C
64
BSS7230 Method F2; Flammability Vertical Direction, 12 Second Ignition, Cure cycle: 5 days at 22°C
Color Cream
Part B
Pink
Part A
Purple
Mixed
Extinguishing Time (sec) 0.7
BSS7230 Method F4; Flammability Horizontal Direction, 15 Second Ignition, Cure cycle: 5 hours at 50°C
0.7
BSS7230 Method F2; Flammability Vertical Direction, 12 Second Ignition, Cure cycle: 5 days at 22°C
0.8
BSS7230 Method F2; Flammability Vertical Direction, 12 Second Ignition, Cure cycle: 5 hours at 50°C
1.1
BSS7230 Method F4; Flammability Horizontal Direction, 15 Second Ignition, Cure cycle: 5 days at 22°C
Slump Properties (mm) 1
25°C; BMS5-28
4
52°C; BMS5-28