Overview of materials for Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.46 - 1.87 g/cc
0.0527 - 0.0676 lb/in³
Average value: 1.66 g/cc Grade Count:45
Filler Content 10.0 - 50.0 %
10.0 - 50.0 %
Average value: 28.3 % Grade Count:23
Water Absorption 0.0200 - 0.0300 %
0.0200 - 0.0300 %
Average value: 0.0225 % Grade Count:12
Additive Loading 20.0 - 30.0 %
20.0 - 30.0 %
Average value: 27.5 % Grade Count:4
Linear Mold Shrinkage 0.000500 - 0.00700 cm/cm
0.000500 - 0.00700 in/in
Average value: 0.00256 cm/cm Grade Count:44
Linear Mold Shrinkage, Transverse 0.00400 - 0.00750 cm/cm
0.00400 - 0.00750 in/in
Average value: 0.00593 cm/cm Grade Count:7
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117 - 121
117 - 121
Average value: 120 Grade Count:6
Tensile Strength, Ultimate 26.2 - 160 MPa
3800 - 23200 psi
Average value: 121 MPa Grade Count:41
Tensile Strength, Yield 131 - 159 MPa
19000 - 23000 psi
Average value: 141 MPa Grade Count:5
Elongation at Break 0.800 - 3.00 %
0.800 - 3.00 %
Average value: 1.74 % Grade Count:43
Modulus of Elasticity 5.86 - 20.0 GPa
850 - 2900 ksi
Average value: 11.6 GPa Grade Count:36
Flexural Yield Strength 45.5 - 221 MPa
6600 - 32000 psi
Average value: 172 MPa Grade Count:42
Flexural Modulus 4.90 - 17.9 GPa
710 - 2600 ksi
Average value: 10.6 GPa Grade Count:42
Compressive Yield Strength 62.1 - 96.5 MPa
9000 - 14000 psi
Average value: 86.9 MPa Grade Count:4
Izod Impact, Notched 0.320 - 0.854 J/cm
0.600 - 1.60 ft-lb/in
Average value: 0.687 J/cm Grade Count:41
Izod Impact, Unnotched 1.07 - 6.94 J/cm
2.00 - 13.0 ft-lb/in
Average value: 3.89 J/cm Grade Count:35
Izod Impact, Notched (ISO) 6.40 - 9.80 kJ/m²
3.05 - 4.66 ft-lb/in²
Average value: 8.53 kJ/m² Grade Count:3
Izod Impact, Unnotched (ISO) 20.0 - 38.5 kJ/m²
9.52 - 18.3 ft-lb/in²
Average value: 28.3 kJ/m² Grade Count:3
Charpy Impact Unnotched 2.50 - 4.50 J/cm²
11.9 - 21.4 ft-lb/in²
Average value: 3.50 J/cm² Grade Count:3
Charpy Impact, Notched 0.600 - 0.850 J/cm²
2.86 - 4.05 ft-lb/in²
Average value: 0.750 J/cm² Grade Count:3
Falling Dart Impact 2.60 - 7.20 J
1.92 - 5.31 ft-lb
Average value: 4.40 J Grade Count:3
Coefficient of Friction 0.140 - 0.440
0.140 - 0.440
Average value: 0.283 Grade Count:7
Coefficient of Friction, Static 0.110 - 0.380
0.110 - 0.380
Average value: 0.263 Grade Count:7
K (wear) Factor 8.50 - 141 x 10-8 mm³/N-M
4.22 - 70.0 x 10-10 in³-min/ft-lb-hr
Average value: 65.2 x 10<sup>-8</sup> mm³/N-M Grade Count:7
Thermal Properties Metric English Comments
CTE, linear 10.8 - 41.4 µm/m-°C
6.00 - 23.0 µin/in-°F
Average value: 24.9 µm/m-°C Grade Count:6
Deflection Temperature at 0.46 MPa (66 psi) 238 - 280 °C
460 - 536 °F
Average value: 263 °C Grade Count:9
Deflection Temperature at 1.8 MPa (264 psi) 232 - 269 °C
450 - 516 °F
Average value: 258 °C Grade Count:41
Vicat Softening Point 255 - 260 °C
491 - 500 °F
Average value: 257 °C Grade Count:3
Flammability, UL94 V-0
V-0
Grade Count:33
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+17 ohm-cm
1.00e+14 - 1.00e+17 ohm-cm
Average value: 1.70e+16 ohm-cm Grade Count:10
Dielectric Constant 3.40
3.40
Average value: 3.40 Grade Count:3
Dielectric Strength 13.8 - 19.7 kV/mm
350 - 500 kV/in
Average value: 15.3 kV/mm Grade Count:4
Dissipation Factor 0.00100
0.00100
Average value: 0.00100 Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 288 - 321 °C
550 - 610 °F
Average value: 304 °C Grade Count:6
Melt Temperature 282 - 343 °C
540 - 650 °F
Average value: 315 °C Grade Count:32
Mold Temperature 51.7 - 177 °C
125 - 350 °F
Average value: 151 °C Grade Count:38
Drying Temperature 121 - 150 °C
250 - 302 °F
Average value: 142 °C Grade Count:30
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:19
Injection Pressure 4.96 - 124 MPa
720 - 18000 psi
Average value: 82.8 MPa Grade Count:29